CN105601107A - Winebottle craft processing technology - Google Patents

Abstract

The invention relates to the field of glass handicraft processing, and concretely relates to a winebottle craft processing technology. The processing technology is characterized in that a cooperation material suitable for product requirement is prepared in a glass winebottle batch workshop, is conveyed to a kiln head bunker of a melting workshop by conveying equipment, then is added in a glass kiln by a charger, is fusion at the high temperature of about 1450 DEG C to glass liquid, the fused glass liquid is supplied to moulding equipment through a material supply channel by a feeding machine to prepare the required product, the product is sent to an annealing furnace by a bottle conveyor and a bottle pusher for annealing to removing stress, examining the quality of the product, packaging the qualified product, and warehousing and delivering.

Description

A kind of bottle handicraft processing technology

Technical field

The present invention relates to Glass Craft manufacture field, concrete is a kind of bottle handicraft processing technology.

Background technology

Glass material has good barrier, can effectively prevent from, between gas, chemical reaction occurs, and also can stop the volatilization of internal gas, has good chemical stability. Therefore the glass wine bottle of producing has advantages of that transparency is high, barrier is strong.

The packaging material of China's wine have much at present, but optimal packaging non-glass bottle does not belong to, and glass wine bottle has the mass conservation that ensures wine that contacts that good barrier can stop inner drinks and extraneous air. Meanwhile, glass wine bottle also has resistance to acid attack and corrosion resistance, therefore, occupies most of share in Wines packing market.

Summary of the invention

The present invention proposes a kind of bottle handicraft processing technology, concrete technical scheme is as follows:

A kind of bottle handicraft processing technology, step is as follows:

1, raw material preprocessing. By block raw material, the raw materials such as such as quartz sand, soda ash, lime stone, feldspar are pulverized, and are moist raw material dryings, iron-bearing material are carried out to deironing processing, to ensure glass quality;

2, batch preparation. By treated raw material, coordinate other material to carry out hybrid process, be that the finished product of glass is more beautiful, firmer;

3, found. Glass batch carries out high-temperature heating in tank furnace or tank furnace, makes it to form evenly, without bubble, and meets the liquid glass of forming requirements;

4, moulding. Liquid glass is put into mould and is made the glassware of required shape;

5, heat treatment. By techniques such as annealing, quenchings, eliminate or produce the stress of inside glass, phase-splitting or crystallization, and the configuration state of change glass.

The batch plant of glass wine bottle is prepared the batch that is applicable to product requirement, be transported to the furnace hopper of melting furnace shop by conveying equipment, then join in glass furnace by charger, high temperature in 1450 degree left and right is fused into glass metal, by the glass metal having melted, supply with former through supply channel by feeding machine again and make required product, through active conveying bottle, bottle pusher etc., product is sent in annealing furnace and annealed and remove stress, after the quality of product is tested, qualified product is packed warehouse-in, is dispatched from the factory.

Detailed description of the invention

A kind of bottle handicraft processing technology, step is as follows:

1, raw material preprocessing. By block raw material, the raw materials such as such as quartz sand, soda ash, lime stone, feldspar are pulverized, and are moist raw material dryings, iron-bearing material are carried out to deironing processing, to ensure glass quality.

2, batch preparation. By treated raw material, coordinate other material to carry out hybrid process, be that the finished product of glass is more beautiful, firmer.

3, found. Glass batch carries out high-temperature heating in tank furnace or tank furnace, makes it to form evenly, without bubble, and meets the liquid glass of forming requirements.

4, moulding. Liquid glass is put into mould and is made the glassware of required shape.

5, heat treatment. By techniques such as annealing, quenchings, eliminate or produce the stress of inside glass, phase-splitting or crystallization, and the configuration state of change glass.

Claims (1)

1. a bottle handicraft processing technology, step is as follows:

1, raw material preprocessing,

By block raw material, the raw materials such as such as quartz sand, soda ash, lime stone, feldspar are pulverized, and are moist raw material dryings, iron-bearing material are carried out to deironing processing, to ensure glass quality;

2, batch preparation,

By treated raw material, coordinate other material to carry out hybrid process, be that the finished product of glass is more beautiful, firmer;

3, found,

Glass batch carries out high-temperature heating in tank furnace or tank furnace, makes it to form evenly, without bubble, and meets the liquid glass of forming requirements;

4, moulding,

Liquid glass is put into mould and is made the glassware of required shape;

5, heat treatment,

By techniques such as annealing, quenchings, eliminate or produce the stress of inside glass, phase-splitting or crystallization, and the configuration state of change glass.