CN105401098A - Abrasion-resistant alloy metallic material - Google Patents
Abrasion-resistant alloy metallic material Download PDFInfo
- Publication number
- CN105401098A CN105401098A CN201510759268.8A CN201510759268A CN105401098A CN 105401098 A CN105401098 A CN 105401098A CN 201510759268 A CN201510759268 A CN 201510759268A CN 105401098 A CN105401098 A CN 105401098A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant alloy
- metallic material
- alloy metallic
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an abrasion-resistant alloy metallic material. The die steel material is prepared from, by weight, 1-5 parts of cobalt, at most 8 parts of nickel, 3-15 parts of copper, 1.3-5.8 parts of chrome, 2-3 parts of phosphorus, 4-6 parts of zinc, 40-50 parts of iron and 10-15 parts of aluminum. The abrasion-resistant alloy metallic material has the beneficial effects that the alloy metallic material is mainly prepared from iron, aluminum and copper, and then other chemical elements are added into the metallic material, so that the abrasion resistance of the metallic material is improved, using is safe and reliable, the service life is prolonged, and the production cost is reduced.
Description
Technical field
The present invention relates to a kind of metallic substance, particularly relate to a kind of wear resistant alloy metallic substance.
Background technology
Wearing and tearing are many industrial sector ubiquities and become the major reason causing equipment failure or material damage, and it also consumes a large amount of energy and material simultaneously.The various engineering excavation manufactured by wear-resistant alloy cast steel and shovel loader bucket tooth, various Wearproof transfer piping, various grinder hammerhead and jaw, various grip-pad, owing to being in the working conditions such as high strength, atrocious weather, its wear pattern is more serious.At present, high-abrasive material general both at home and abroad still based on iron and steel, mainly comprise high mangaenese steel, alloy hundred white iron and in, low wear-resisting alloy steel.China is the country of the few chromium of scarce nickel, and wearing piece production aggregate level falls behind, and material wear ability is general, the easy fracture damage of material, and energy consumption is high, and environmental pollution is serious, if adopt a large amount of precious metal to improve production cost.
Therefore, for solving the problem, spy provides a kind of new technical scheme.
Summary of the invention
The invention provides a kind of wear resistant alloy metallic substance.
The technical solution used in the present invention is:
A kind of wear resistant alloy metallic substance, the composition of this die steel material and weight part are:
Cobalt 1-5 part;
Maximum 8 parts of nickel;
Copper is from being greater than 3 to 15 parts;
Chromium is from being greater than 1.3 to 5.8 parts;
Phosphorus 2-3 part;
Zinc 4-6 part;
Iron 40-50 part;
Aluminium 10-15 part.
Further, containing the copper of at least 3.58 parts.
Further, the copper of 13.5 parts is at the most contained.
Further, containing the chromium of at least 1.45 parts.
Further, the weight part of described iron is 42-44 part.
Further, the weight part of described aluminium is 11-14.5 part.
The invention has the beneficial effects as follows: this alloy metal material primarily of iron, aluminium and copper composition, then adds all the other chemical elements, enhances the wear resistance of metallic substance, safe and reliable, extends work-ing life, reduces production cost.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment, only for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of wear resistant alloy metallic substance, the composition of this die steel material and weight part are:
Cobalt 1 part;
1 part, nickel;
Copper 3 parts;
Chromium 1.3 parts;
2 parts, phosphorus;
4 parts, zinc;
Iron 40 parts;
10 parts, aluminium.
Embodiment 2
A kind of wear resistant alloy metallic substance, the composition of this die steel material and weight part are:
Cobalt 3 parts;
4 parts, nickel;
Copper 8 parts;
Chromium 3.5 parts;
2.5 parts, phosphorus;
5 parts, zinc;
Iron 45 parts;
12.5 parts, aluminium.
Embodiment 3
A kind of wear resistant alloy metallic substance, the composition of this die steel material and weight part are:
Cobalt 5 parts;
8 parts, nickel;
Copper 15 parts;
Chromium 5.8 parts;
3 parts, phosphorus;
6 parts, zinc;
Iron 50 parts;
15 parts, aluminium.
The invention has the beneficial effects as follows: this alloy metal material primarily of iron, aluminium and copper composition, then adds all the other chemical elements, enhances the wear resistance of metallic substance, safe and reliable, extends work-ing life, reduces production cost.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (6)
1. a wear resistant alloy metallic substance, is characterized in that: the composition of this die steel material and weight part are:
Cobalt 1-5 part;
Maximum 8 parts of nickel;
Copper is from being greater than 3 to 15 parts;
Chromium is from being greater than 1.3 to 5.8 parts;
Phosphorus 2-3 part;
Zinc 4-6 part;
Iron 40-50 part;
Aluminium 10-15 part.
2. a kind of wear resistant alloy metallic substance according to claim 1, is characterized in that: containing the copper of at least 3.58 parts.
3. a kind of wear resistant alloy metallic substance according to claim 1, is characterized in that: the copper containing 13.5 parts at the most.
4. a kind of wear resistant alloy metallic substance according to claim 1, is characterized in that: containing the chromium of at least 1.45 parts.
5. a kind of wear resistant alloy metallic substance according to claim 1, is characterized in that: the weight part of described iron is 42-44 part.
6. a kind of wear resistant alloy metallic substance according to claim 1, is characterized in that: the weight part of described aluminium is 11-14.5 part.