CN105153818A - Pencil core produced from straws - Google Patents
Pencil core produced from straws Download PDFInfo
- Publication number
- CN105153818A CN105153818A CN201510582008.8A CN201510582008A CN105153818A CN 105153818 A CN105153818 A CN 105153818A CN 201510582008 A CN201510582008 A CN 201510582008A CN 105153818 A CN105153818 A CN 105153818A
- Authority
- CN
- China
- Prior art keywords
- stalk
- pencil
- lead
- graphite
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the fields of production and processing of pencils and particularly relates to a pencil core produced from straws. The pencil core is characterized by comprising the following components in parts by weight: 70-80 parts of straws, 30-40 parts of graphite and 15-25 parts of an adhesive. According to the pencil core, the content of carbon in ash produced after the straws are heated in an oxygen insulation manner is 40%, other contents such as silicon, potassium chloride and calcium can be utilized as the components of clay, and therefore, the ash can be integrally utilized; energy sources are saved, the cost is lowered, the straw resource is reasonably utilized, the produced pencil core can be utilized for smoothly writing, and dreg dropping is avoided.
Description
Technical field:
The present invention relates to the process for processing field of pencil, more specifically to the pencil-lead that a kind of stalk manufactures.
Background technology:
Stalk is the general name of ripe farm crop cauline leaf (fringe) part.Be often referred to wheat, paddy rice, corn, potato class, rape, cotton, sugarcane and other farm crop (the being generally coarse food grain) remainder after results seed.The photosynthetic product of farm crop has and is over halfly present in stalk, and stalk is rich in carbon, nitrogen, phosphorus, potassium, calcium, magnesium and organic matter etc., is that one has multiduty reproducible Biological resources.
Summary of the invention:
Technical problem to be solved by this invention is to overcome the pencil-lead that existing technological deficiency provides a kind of stalk to manufacture.
Technical problem to be solved by this invention adopts following technical scheme to realize:
With the pencil-lead that stalk manufactures, it is characterized in that: it comprises stalk, graphite and tackiness agent, component is by weight: stalk 70-80 part, graphite 30-40 part, tackiness agent 15-25 part.
A making method for the pencil-lead that stalk manufactures, is characterized in that comprising the following steps:
(1) stalk is carried out pre-treatment, heat under sealing oxygen barrier environment, obtain ash content, Heating temperature is 500 DEG C, and the time is 3 hours;
(2) graphite is ground to form fine powder, add solvent after weighing with ash content, tackiness agent and mix under normal temperature condition;
(3) after mixing through mediating, roll-in rear panel is broken, play excellent extrusion molding;
(4) after pressing core, cutting core, carry out rotary drying again after extrusion molding, after drying, fill crucible, enter in roasting furnace to enter after roast and burn core stove burning core;
(5) clean through oil immersion, after drying, make pencil-lead.
Further, described solvent is the alcohol of concentration 70%.
Further, the oil used in described oil immersion process comprises the component of following weight part: the sesame oil of the ethanol of 60-70 part, the paraffin of 20-30 part, 30-40 part.
In the ash content produced after stalk oxygen barrier heating of the present invention, the content of carbon occupies 40%, other contain some can utilize as the composition of clay as silicon, Repone K, calcium composition, such ash content just can entirety utilize, present invention saves the energy, reduce cost, reasonably make use of stalk resource, the pencil-lead fluent writing produced, without falling slag.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1: the pencil-lead manufactured with stalk, it is characterized in that: it comprises stalk, graphite and tackiness agent, component is by weight: stalk 80 parts, 40 parts, graphite, tackiness agent 25 parts.
A making method for the pencil-lead that stalk manufactures, is characterized in that comprising the following steps:
(1) stalk is carried out pre-treatment, heat under sealing oxygen barrier environment, obtain ash content, Heating temperature is 500 DEG C, and the time is 3 hours;
(2) graphite is ground to form fine powder, add solvent after weighing with ash content, tackiness agent and mix under normal temperature condition;
(3) after mixing through mediating, roll-in rear panel is broken, play excellent extrusion molding;
(4) after pressing core, cutting core, carry out rotary drying again after extrusion molding, after drying, fill crucible, enter in roasting furnace to enter after roast and burn core stove burning core;
(5) clean through oil immersion, after drying, make pencil-lead.
Solvent is the alcohol of concentration 70%.
The oil used in oil immersion process comprises the component of following weight part: the ethanol of 70 parts, the paraffin of 30 parts, the sesame oil of 40 parts.
Embodiment 2: the pencil-lead manufactured with stalk, it is characterized in that: it comprises stalk, graphite and tackiness agent, component is by weight: stalk 70 parts, 30 parts, graphite, tackiness agent 15 parts.
A making method for the pencil-lead that stalk manufactures, is characterized in that comprising the following steps:
(1) stalk is carried out pre-treatment, heat under sealing oxygen barrier environment, obtain ash content, Heating temperature is 500 DEG C, and the time is 3 hours;
(2) graphite is ground to form fine powder, add solvent after weighing with ash content, tackiness agent and mix under normal temperature condition;
(3) after mixing through mediating, roll-in rear panel is broken, play excellent extrusion molding;
(4) after pressing core, cutting core, carry out rotary drying again after extrusion molding, after drying, fill crucible, enter in roasting furnace to enter after roast and burn core stove burning core;
(5) clean through oil immersion, after drying, make pencil-lead.
Solvent is the alcohol of concentration 70%.
The oil used in oil immersion process comprises the component of following weight part: the ethanol of 60 parts, the paraffin of 20 parts, the sesame oil of 30 parts.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1., with the pencil-lead that stalk manufactures, it is characterized in that: it comprises stalk, graphite and tackiness agent, component is by weight: stalk 70-80 part, graphite 30-40 part, tackiness agent 15-25 part.
2., by a making method for the pencil-lead of stalk manufacture, it is characterized in that comprising the following steps:
(1) stalk is carried out pre-treatment, heat under sealing oxygen barrier environment, obtain ash content, Heating temperature is 500 DEG C, and the time is 3 hours;
(2) graphite is ground to form fine powder, add solvent after weighing with ash content, tackiness agent and mix under normal temperature condition;
(3) after mixing through mediating, roll-in rear panel is broken, play excellent extrusion molding;
(4) after pressing core, cutting core, carry out rotary drying again after extrusion molding, after drying, fill crucible, enter in roasting furnace to enter after roast and burn core stove burning core;
(5) clean through oil immersion, after drying, make pencil-lead.
3. the making method of the pencil-lead of a kind of stalk manufacture according to claim 2, is characterized in that: described solvent is the alcohol of concentration 70%.
4. the making method of the pencil-lead of a kind of stalk manufacture according to claim 2, is characterized in that the oil used in described oil immersion process comprises the component of following weight part: the sesame oil of the ethanol of 60-70 part, the paraffin of 20-30 part, 30-40 part.