CN104987772A - Printing slurry - Google Patents
Printing slurry Download PDFInfo
- Publication number
- CN104987772A CN104987772A CN201510359987.0A CN201510359987A CN104987772A CN 104987772 A CN104987772 A CN 104987772A CN 201510359987 A CN201510359987 A CN 201510359987A CN 104987772 A CN104987772 A CN 104987772A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing slurry
- mixed solution
- stir
- turns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to printing slurry. The printing slurry comprises, by weight, 10 parts to 30 parts of acetyl tributyl citrate, 15 parts to 40 parts of calcium carbonate, 20 parts to 50 parts of antimonous oxide, 10 parts to 25 parts of polyacrylamide, 10 parts to 30 parts of ethanediol, 10 parts to 25 parts of titanium dioxide powder, 20 parts to 35 parts of terpilenol and 20 parts to 30 parts of ethyl alcohol. By means of the printing slurry, harmful substances jeopardizing the health of the human body can be avoided in the follow-up use process of printed products; meanwhile, environment pollution can be avoided, and environment protection is facilitated.
Description
Technical field
The present invention relates to print field, be specifically related to a kind of printing slurry.
Background technology
Must use in printing slurry printing, existing printing slurry is of a great variety, but many printing slurries all exist harmful composition, causes print product to be detrimental to health in follow-up use procedure, is also unfavorable for the protection of environment simultaneously.
Summary of the invention
In sum, for solving prior art problem, technical problem to be solved by this invention is to provide a kind of printing slurry.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of printing slurry, comprises each component of following parts by weight: tributyl acetylcitrate 10-30 part, calcium carbonate 15-40 part, antimonous oxide 20-50 part, poly amic acid 10-25 part, ethylene glycol 10-30 part, titanium dioxide powder 10-25 part, Terpineol 350 20-35 part and ethanol 20-30 part.
A making method for printing slurry, comprises following making step:
(1) component of following parts by weight is taken respectively: tributyl acetylcitrate 10-30 part, calcium carbonate 15-40 part, antimonous oxide 20-50 part, poly amic acid 10-25 part, ethylene glycol 10-30 part, titanium dioxide powder 10-25 part, Terpineol 350 20-35 part and ethanol 20-30 part;
(2) mixing step (1) take and stir titanium dioxide powder, Terpineol 350 and ethanol, and to stir, obtain first mixed solution;
(3) the first mixed solution that mixing step (1) takes antimonous oxide, poly amic acid, ethylene glycol and step (2) obtain, and stir, obtain secondary mixed solution;
(4) the secondary mixed solution that mixing step (1) obtains tributyl acetylcitrate, calcium carbonate and step (3) obtain, and stir, can printing slurry be obtained.
Further, the stirring velocity of step (2) is per minute 200 turns, and churning time is 1 hour.
Further, the stirring velocity of step (3) is per minute 300 turns, and churning time is 1.5 hours.
Further, the stirring velocity of step (4) is per minute 100 turns, and churning time is 0.5 hour.
The invention has the beneficial effects as follows: a kind of printing slurry provided by the invention, can not the objectionable impurities be detrimental to health be produced in the process of the follow-up use of print product, the pollution of environment can not be caused simultaneously, be conducive to environmental protection.
Embodiment
Be described principle of the present invention and feature below in conjunction with specific examples, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1
A making method for printing slurry, comprises following making step:
(1) component of following parts by weight is obtained respectively: tributyl acetylcitrate 10 parts, 15 parts, calcium carbonate, antimonous oxide 20 parts, poly amic acid 10 parts, ethylene glycol 10 parts, titanium dioxide powder 10 parts, Terpineol 350 20 parts and ethanol 20 parts;
(2) titanium dioxide powder, Terpineol 350 and the ethanol that obtain of mixing step (1), and stir, wherein stirring velocity is per minute 200 turns, and churning time is 1 hour, obtains first mixed solution after stirring;
(3) the first mixed solution that mixing step (1) obtains antimonous oxide, poly amic acid, ethylene glycol and step (2) obtain, and stir, wherein stirring velocity is per minute 300 turns, and halved temporal is 1.5 hours, obtains secondary mixed solution after stirring;
(4) the secondary mixed solution that mixing step (1) obtains tributyl acetylcitrate, calcium carbonate and step (3) obtain, and stir, wherein stirring velocity is per minute 100 turns, and halved temporal is 0.5 hour, can obtain printing slurry after stirring.
Embodiment 2
A making method for printing slurry, comprises following making step:
(1) component of following parts by weight is obtained respectively: tributyl acetylcitrate 20 parts, 30 parts, calcium carbonate, antimonous oxide 30 parts, poly amic acid 20 parts, ethylene glycol 20 parts, titanium dioxide powder 20 parts, Terpineol 350 30 parts and ethanol 25 parts;
(2) titanium dioxide powder, Terpineol 350 and the ethanol that obtain of mixing step (1), and stir, wherein stirring velocity is per minute 200 turns, and churning time is 1 hour, obtains first mixed solution after stirring;
(3) the first mixed solution that mixing step (1) obtains antimonous oxide, poly amic acid, ethylene glycol and step (2) obtain, and stir, wherein stirring velocity is per minute 300 turns, and halved temporal is 1.5 hours, obtains secondary mixed solution after stirring;
(4) the secondary mixed solution that mixing step (1) obtains tributyl acetylcitrate, calcium carbonate and step (3) obtain, and stir, wherein stirring velocity is per minute 100 turns, and halved temporal is 0.5 hour, can obtain printing slurry after stirring.
Embodiment 3
A making method for printing slurry, comprises following making step:
(1) component of following parts by weight is obtained respectively: tributyl acetylcitrate 30 parts, 40 parts, calcium carbonate, antimonous oxide 50 parts, poly amic acid 25 parts, ethylene glycol 30 parts, titanium dioxide powder 25 parts, Terpineol 350 35 parts and ethanol 30 parts;
(2) titanium dioxide powder, Terpineol 350 and the ethanol that obtain of mixing step (1), and stir, wherein stirring velocity is per minute 200 turns, and churning time is 1 hour, obtains first mixed solution after stirring;
(3) the first mixed solution that mixing step (1) obtains antimonous oxide, poly amic acid, ethylene glycol and step (2) obtain, and stir, wherein stirring velocity is per minute 300 turns, and halved temporal is 1.5 hours, obtains secondary mixed solution after stirring;
(4) the secondary mixed solution that mixing step (1) obtains tributyl acetylcitrate, calcium carbonate and step (3) obtain, and stir, wherein stirring velocity is per minute 100 turns, and halved temporal is 0.5 hour, can obtain printing slurry after stirring.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. a printing slurry, it is characterized in that, comprise each component of following parts by weight: tributyl acetylcitrate 10-30 part, calcium carbonate 15-40 part, antimonous oxide 20-50 part, poly amic acid 10-25 part, ethylene glycol 10-30 part, titanium dioxide powder 10-25 part, Terpineol 350 20-35 part and ethanol 20-30 part.
2. a making method for printing slurry, is characterized in that, comprises following making step:
(1) component of following parts by weight is taken respectively: tributyl acetylcitrate 10-30 part, calcium carbonate 15-40 part, antimonous oxide 20-50 part, poly amic acid 10-25 part, ethylene glycol 10-30 part, titanium dioxide powder 10-25 part, Terpineol 350 20-35 part and ethanol 20-30 part;
(2) titanium dioxide powder, Terpineol 350 and the ethanol that take of mixing step (1), and stir, obtain first mixed solution;
(3) the first mixed solution that mixing step (1) takes antimonous oxide, poly amic acid, ethylene glycol and step (2) obtain, and stir, obtain secondary mixed solution;
(4) the secondary mixed solution that mixing step (1) takes tributyl acetylcitrate, calcium carbonate and step (3) obtain, and stir, can printing slurry be obtained.
3. the making method of a kind of printing slurry according to claim 2, is characterized in that, the stirring velocity of step (2) is per minute 200 turns, and churning time is 1 hour.
4. the making method of a kind of printing slurry according to claim 2, is characterized in that, the stirring velocity of step (3) is per minute 300 turns, and churning time is 1.5 hours.
5. the making method of a kind of printing slurry according to claim 2, is characterized in that, the stirring velocity of step (4) is per minute 100 turns, and churning time is 0.5 hour.