CN104803639A - 一种保温隔音型植物纤维水泥复合条板及其制作方法 - Google Patents
一种保温隔音型植物纤维水泥复合条板及其制作方法 Download PDFInfo
- Publication number
- CN104803639A CN104803639A CN201510146713.3A CN201510146713A CN104803639A CN 104803639 A CN104803639 A CN 104803639A CN 201510146713 A CN201510146713 A CN 201510146713A CN 104803639 A CN104803639 A CN 104803639A
- Authority
- CN
- China
- Prior art keywords
- parts
- plant fiber
- cement
- minute
- batten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种保温隔音型植物纤维水泥复合条板，由下列重量份的原料制成：植物纤维20-30、硅酸盐水泥25-35、粉煤灰40-45、聚丙烯纤维5-8、膨胀珍珠岩10-13、热塑性淀粉4-7、硼砂1-3、甲酸钙0.7-0.9、木质素磺酸盐0.4-0.7、聚四氟乙烯乳液15-18、二甲基丙烯酸乙二醇酯7-11、废机油3-6、水适量；本发明的植物纤维水泥复合条板具有保温、隔音、密实性强、渗透性好、成本低等优点，提高了植物纤维的综合利用水平，降低因废弃资源处理不当造成的严重损害。
Description
技术领域
本发明涉及建筑材料料技术领域，具体涉及一种保温隔音型植物纤维水泥复合条板及其制作方法。
背景技术
进入90年代以来，在对居住环境的选择上，人们已不满足于一般的有其居，而是在追求具有天然特性的建筑材料即环境协调型新建材。环境协调型建材必须满足保温节能、吸声隔音、耐水防火、无毒无味、轻质、高强、安全等特性，植物纤维水泥复合条板就是一种新型的环境协调型建筑材料，所选用的植物纤维是指一年生植物纤维，主要指农作物秸秆如玉米杆、麦杆、棉花杆、麻杆等。
在我国一年生植物产量丰富，是取之不尽、用之不竭的原料，它们的生命期较短，枯死后没有太大用途。这些农作物秸秆经切断锤碎后制得的植物纤维特点是长径比大、比强度高、比表面积大、密度低及可生物降解，此外还具有成本低、抗拉强度高等优点，代替木材作水泥复合条板增强材料，在使用过程中无有害物质和有害气体生成。
但植物纤维萃取物对水泥的阻凝作用及水泥水化物的碱性侵蚀作用均限制了植物纤维水泥复合条板的应用，表现在：水泥基材孔隙中的高碱性液相对植物纤维具有侵蚀作用，从而影响复合条板的耐久性；植物纤维具有很高的吸水率，会引起体积变化导致植物纤维水泥复合条板受潮后弯拉强度与弹性模量的大幅下降，使复合条板发生扭曲变形，甚至开裂；植物纤维在微生物作用下因发生解聚，使其聚合度下降并导致其抗拉强度相应降低。为解决现有技术中的问题，需要对现有植物纤维表面进行改性处理和降低胶凝材料的碱性。
发明内容
本发明的目的就是提供一种保温隔音型植物纤维水泥复合条板及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种保温隔音型植物纤维水泥复合条板，其特征在于，由下列重量份的原料制成：植物纤维20-30、硅酸盐水泥25-35、粉煤灰40-45、聚丙烯纤维5-8、膨胀珍珠岩10-13、热塑性淀粉4-7、硼砂1-3、甲酸钙0.7-0.9、木质素磺酸盐0.4-0.7、聚四氟乙烯乳液15-18、二甲基丙烯酸乙二醇酯7-11、废机油3-6、水适量。
所述的一种保温隔音型植物纤维水泥复合条板的制备方法，其特征在于包括以下步骤：
（1）将植物纤维放入105℃的烘箱内约3-4小时烘干，室温晾干，再用皮锤轻敲至果胶清除并粉碎至直径为3-6mm，将其置于质量浓度为10%的聚四氟乙烯乳液中浸泡24小时，压干后烘干，鼓风至翻腾状态喷入雾状废机油，烘干；
（2）将膨胀珍珠岩于570-680℃下煅烧1-2小时，冷却加入粉煤灰、热塑性淀粉搅拌研磨30-40分钟，加入硼砂升温至150-200℃搅拌5-10分钟，降温至50-80℃，加入二甲基丙烯酸乙二醇酯继续搅拌3-5分钟，冷却至室温，烘干研细；
（3）将甲酸钙加水溶解并搅拌10-15分钟，加入步骤（1）、（2）反应物料搅拌混匀，再加入硅酸盐水泥及其他剩余成分搅拌20-30分钟，加入成型机成型，20-30h后依次经切割、脱模、自然 养护得到成品。
本发明有以下有益效果：本发明制备简单操作简便，首先采取聚四氟乙烯乳液浸渍处理工艺对植物纤维表面预处理使得植物纤维的内外表面包裹有一层聚合物薄膜，干燥后聚合物固化，再喷洒雾状废机油，使整根纤维密实并获得一定的刚性，且耐水性得到改善；其次添加粉煤灰并加以改性取代部分水泥，减少水化后氢氧化钙的生成量，改善植物纤维的抗腐蚀性能，同时选取0.42的水灰比，制得的植物纤维水泥复合条板具有保温、隔音、密实性强、渗透性好、成本低等优点，提高了植物纤维的综合利用水平，降低因废弃资源处理不当造成的严重损害。
具体实施方式
所述的一种保温隔音型植物纤维水泥复合条板，其特征在于，由下列重量份的原料制成：植物纤维28、硅酸盐水泥30、粉煤灰44、聚丙烯纤维5、膨胀珍珠岩11、热塑性淀粉6、硼砂1、甲酸钙0.8、木质素磺酸盐0.5、聚四氟乙烯乳液17、二甲基丙烯酸乙二醇酯9、废机油4、水适量。
制作方法包括以下步骤：
（1）将植物纤维放入105℃的烘箱内约3-4小时烘干，室温晾干，再用皮锤轻敲至果胶清除并粉碎至直径为3-6mm，将其置于质量浓度为10%的聚四氟乙烯乳液中浸泡24小时，压干后烘干，鼓风至翻腾状态喷入雾状废机油，烘干；
（2）将膨胀珍珠岩于570-680℃下煅烧1-2小时，冷却加入粉煤灰、热塑性淀粉搅拌研磨30-40分钟，加入硼砂升温至150-200℃搅拌5-10分钟，降温至50-80℃，加入二甲基丙烯酸乙二醇酯继续搅拌3-5分钟，冷却至室温，烘干研细；
（3）将甲酸钙加水溶解并搅拌10-15分钟，加入步骤（1）、（2）反应物料搅拌混匀，再加入硅酸盐水泥及其他剩余成分搅拌20-30分钟，加入成型机成型，20-30h后依次经切割、脱模、自然 养护得到成品。
使用本发明生产的植物纤维水泥复合条板的技术参数指标如下：
（1）养护28d的劈裂抗拉强度提高了21.5%；
（2）养护28d的抗弯强度提高了14.6%；
（3）导热系数（平均温度25±2℃）：0.082W/(m·k)；
（4）吸声系数最高值为0.688，隔音量为24dB。
Claims (2)
1.一种保温隔音型植物纤维水泥复合条板，其特征在于，由下列重量份的原料制成：植物纤维20-30、硅酸盐水泥25-35、粉煤灰40-45、聚丙烯纤维5-8、膨胀珍珠岩10-13、热塑性淀粉4-7、硼砂1-3、甲酸钙0.7-0.9、木质素磺酸盐0.4-0.7、聚四氟乙烯乳液15-18、二甲基丙烯酸乙二醇酯7-11、废机油3-6、水适量。
2.根据权利要求1所述的一种保温隔音型植物纤维水泥复合条板的制作方法，其特征在于包括以下步骤：
（1）将植物纤维放入105℃的烘箱内约3-4小时烘干，室温晾干，再用皮锤轻敲至果胶清除并粉碎至直径为3-6mm，将其置于质量浓度为10%的聚四氟乙烯乳液中浸泡24小时，压干后烘干，鼓风至翻腾状态喷入雾状废机油，烘干；
（2）将膨胀珍珠岩于570-680℃下煅烧1-2小时，冷却加入粉煤灰、热塑性淀粉搅拌研磨30-40分钟，加入硼砂升温至150-200℃搅拌5-10分钟，降温至50-80℃，加入二甲基丙烯酸乙二醇酯继续搅拌3-5分钟，冷却至室温，烘干研细；
（3）将甲酸钙加水溶解并搅拌10-15分钟，加入步骤（1）、（2）反应物料搅拌混匀，再加入硅酸盐水泥及其他剩余成分搅拌20-30分钟，加入成型机成型，20-30h后依次经切割、脱模、自然 养护得到成品。