CN104130551A - 环状聚酯cbt/木塑复合材料 - Google Patents

环状聚酯cbt/木塑复合材料 Download PDF

Info

Publication number
CN104130551A
CN104130551A CN201410351724.0A CN201410351724A CN104130551A CN 104130551 A CN104130551 A CN 104130551A CN 201410351724 A CN201410351724 A CN 201410351724A CN 104130551 A CN104130551 A CN 104130551A
Authority
CN
China
Prior art keywords
plastic composite
composite material
wood plastic
cyclic polyester
cbt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410351724.0A
Other languages
English (en)
Other versions
CN104130551B (zh
Inventor
宋剑斌
杨文斌
徐建锋
文月琴
郑峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Agriculture and Forestry University
Original Assignee
Fujian Agriculture and Forestry University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Agriculture and Forestry University filed Critical Fujian Agriculture and Forestry University
Priority to CN201410351724.0A priority Critical patent/CN104130551B/zh
Publication of CN104130551A publication Critical patent/CN104130551A/zh
Application granted granted Critical
Publication of CN104130551B publication Critical patent/CN104130551B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及木塑复合材料的技术领域，更具体的涉及一种环状聚酯CBT/木塑复合材料。所述木塑复合材料的原料各质量配比为：环状聚酯CBT占40%~70%、聚氨酯PU占0%~30%，竹粉占30%。该配方生产的木塑复合材料其力学性能远远高于目前市场上的木塑复合材料。与此同时，利用该配方生产的木塑复合材料不会改变现有的木塑复合材料生产工艺，具有很好的应用前景。

Description

环状聚酯CBT/木塑复合材料
技术领域
    本发明涉及木塑复合材料的技术领域，更具体的涉及一种环状聚酯CBT/木塑复合材料。
背景技术
    目前，传统的木塑复合材料基本上是以通用塑料聚烯烃（PE, PP, PVC）为主要基体树脂，其拉伸强度，弯曲强度等较低，只能用作装饰装修材料，无法作为结构材料使用，而性能优异的工程塑料（PC，PBT）等因其高的加工温度无法在木塑复合材料中得到应用。
发明内容
本发明的目的在于提供一种高性能的环状聚酯CBT/木塑复合材料，可大大提高木塑复合材料的力学性能，扩大了木塑复合材料的应用范围。
本发明的环状聚酯CBT/木塑复合材料，其原料各质量配比为：环状聚酯CBT 占 40% ~ 70%、聚氨酯PU占0% ~ 30%，竹粉占30%，上述各质量百分比之和为100%。
优选地，所述复合材料的原料各质量配比为：环状聚酯CBT 占65%、聚氨酯PU占5%，竹粉占30%。
所述竹粉的粒度为100目。
该复合材料弯曲强度可达93.5 MPa，拉伸强度最高可达46.5MPa。 
    本发明的木塑复合材料其力学性能远远高于目前市场上的木塑复合材料，具有很好的使用性能，与此同时，利用该配方生产的木塑复合材料不会改变现有的木塑复合材料生产工艺。
附图说明
图1为CBT/木塑复合材料的拉伸强度随聚氨酯含量的变化曲线图
图2为CBT/木塑复合材料的弯曲强度随聚氨酯含量的变化曲线图。
图3为CBT/木塑复合材料的缺口冲击强度随聚氨酯含量的变化曲线图。
具体实施方式
   实施例1：
环状聚酯CBT/木塑复合材料，所述材料的原料各重量配比为：环状聚酯CBT 7.0 kg、聚氨酯PU（聚乙烯）0 kg、竹粉 3.0 kg，所述竹粉经过100oC干燥24h，粒径100目。
实施例2：
环状聚酯CBT/木塑复合材料，所述材料的原料各重量配比为：环状聚酯CBT 6.5 kg、聚氨酯PU（聚乙烯）0.5 kg、竹粉 3.0 kg，所述竹粉经过100oC干燥24h，粒径100目。
实施例3：
环状聚酯CBT/木塑复合材料，所述材料的原料各重量配比为：环状聚酯CBT 5.5 kg、聚氨酯PU（聚乙烯或聚丙烯）1.5 kg、竹粉 3.0 kg，所述竹粉经过100oC干燥24h，粒径100目。
实施例4：
环状聚酯CBT/木塑复合材料，所述材料的原料各重量配比为：环状聚酯CBT 4.0 kg、聚氨酯PU（聚乙烯或聚丙烯）3.0 kg、竹粉 3.0 kg，所述竹粉经过100 oC干燥24h，粒径100目。
采用上述原料制备环状聚酯CBT/木塑复合材料的工艺过程为：
1．密炼
将实施例1-4称量好的CBT和竹粉放入密炼机中进行熔融共混，温度为160 oC、共混时间为5min。
2. 粉碎及混合
 将上述混合物放入塑料粉碎机中，进行粉碎，时间2 min。然后将混合物取放入混合机中，再加入定量的聚氨酯，再混合5 min。
3. 成型
将上述混合料送入注塑机中，根据模具要求直接注塑成型。注塑温度为180oC，压力110 bar左右。
4．修边
对成品进行修边处理。
5. 环状聚酯CBT/木塑复合材料物理性能
CBT/木塑复合材料的拉伸强度、弯曲强度和缺口冲击强度测试分别按照标准ISO 527-2:1993、ISO 178:2001和ISO 180: 2000 进行，获得结果如图1、2、3所示。
图1，当PU添加量为5%时，竹粉与PBT（聚合后的CBT）之间的界面结合力得以增强，因此拉伸强度最高。当PU添加量继续增加时，复合材料的拉伸强度却逐渐下降。这主要是因为随着柔性的PU量的增加，PBT（聚合后的CBT）的刚性大幅度下降的原因。
图2，同样是在5%的PU添加量时弯曲强度达到最大。这主要是因为CBT聚合后变为PBT，其具有刚性，此外，由于添加了一定量的的PU，改善了竹粉与PBT之间的界面结合状态，有效地传递了应力。但是，当PU添加量继续增加时，复合材料的弯曲强度也跟着下降，这说明复合材料的刚性会由于PU量的增加而下降。
图3，PU是弹性体，因此，随着其含量的增加，复合材料的冲击韧性也增加。

Claims (3)

1.一种环状聚酯CBT/木塑复合材料，其特征在于：所述复合材料的原料各质量配比为：环状聚酯CBT 占 40% ~ 70%、聚氨酯PU占0% ~ 30%，竹粉占30%，上述各质量百分比之和为100%。
2.根据权利要求1所述环状聚酯CBT/木塑复合材料，其特征在于：所述竹粉的粒度为100目。
3.根据权利要求1所述环状聚酯CBT/木塑复合材料，其特征在于：所述复合材料的原料各质量配比为：环状聚酯CBT 占65%、聚氨酯PU占5%，竹粉占30%。
CN201410351724.0A 2014-07-23 2014-07-23 环状聚酯cbt/木塑复合材料 Expired - Fee Related CN104130551B (zh)