BE1029420B1 - MASONRY MORTAR COMPOSITION - Google Patents
MASONRY MORTAR COMPOSITION Download PDFInfo
- Publication number
- BE1029420B1 BE1029420B1 BE20215407A BE202105407A BE1029420B1 BE 1029420 B1 BE1029420 B1 BE 1029420B1 BE 20215407 A BE20215407 A BE 20215407A BE 202105407 A BE202105407 A BE 202105407A BE 1029420 B1 BE1029420 B1 BE 1029420B1
- Authority
- BE
- Belgium
- Prior art keywords
- masonry mortar
- mortar composition
- masonry
- less
- composition according
- Prior art date
Abstract
Deze uitvinding betreft een metselmortelsamenstelling voor metselmortel, omvattende tussen 5 en 25 w% anorganisch bindmiddel, waarbij dit bindmiddel bestaat uit calcium aluminaat cement, waarbij dit calcium aluminaat cement omvat: - tussen 30 w% en 80 w% Al2O3; - minder dan 0,1 w% Cl-; - minder dan 0,4 w% alkali; - minder dan 0,3 w% SO3. Daarnaast betreft deze uitvinding een samenstel van een metselmortel met een dergelijke metselmortelsamenstelling en bakstenen. Verder betreft deze uitvinding ook metselwerk opgetrokken met een dergelijk samenstel.This invention relates to a masonry mortar composition for masonry mortar, comprising between 5 and 25 wt% inorganic binder, this binder consisting of calcium aluminate cement, wherein this calcium aluminate cement comprises: - between 30 wt% and 80 wt% Al2O3; - less than 0.1 w% Cl-; - less than 0.4 wt% alkali; - less than 0.3 w% SO3. In addition, this invention relates to an assembly of a masonry mortar with such a masonry mortar composition and bricks. Furthermore, this invention also relates to masonry erected with such an assembly.
Description
METSELMORTELSAMENSTELLING Deze uitvinding heeft betrekking op een metselmortelsamenstelling voor metselmortel en op een samenstel van een metselmortel met een dergelijke metselmortelsamenstelling en bakstenen voor het optrekken van metselwerk. Met metselmortel wordt hier mortel volgens EN 998-2 bedoeld. De uitvinding is van toepassing op zowel de hierin beschreven types G (prestatie metselmortel), T en L. Dergelijke metselmortel kent verschillende toepassingen en is typisch bedoeld om hiermee in combinatie met gevelstenen een gevel op te trekken. Met metselwerk wordt metselwerk bedoeld dat opgetrokken is volgens de goede bouwpraktijken, zoals beschreven in Infoblad 45 — Uitvoeringsrichtlijn baksteenmetselwerk van KNB, december 2015 en in uitgave TV271 van het WTCB, februari 2020.MASONRY MORTAR COMPOSITION This invention relates to a masonry mortar composition for masonry mortar and to an assembly of a masonry mortar with such a masonry mortar composition and bricks for erecting masonry. Masonry mortar here refers to mortar according to EN 998-2. The invention applies to both the types G (performance masonry mortar), T and L described herein. Such masonry mortar has various applications and is typically intended to be used in combination with facing bricks to erect a facade. Brickwork is defined as brickwork constructed in accordance with good building practices, as described in Info sheet 45 — Brick masonry implementation guideline of the KNB, December 2015 and in edition TV271 of the BBRI, February 2020.
Een gekend probleem bij bestaande metselmortels die gebruikt worden om hiermee metselwerk op te trekken, is het voorkomen van late uitbloeiingen, die hardnekkig en blijvend van aard zijn en die een lichte, witgrijze waas vertonen op het oppervlak. Typisch voor dit type uitbloeiingen is dat ze enkel verschijnen na enkele maanden of zelfs maar na één of twee jaar na voltooiing van het gebouw. De efflorescentie waarvan hier sprake, kan bestaan uit al dan niet gehydrateerde vormen van CaSO4, en eventueel ook nog als dubbelzouten met andere kationen zoals Na, K of Mg, of in combinatie met CaCO:. Deze uitbloeiingen worden typisch omschreven als late gipsuitbloeiingen, zoals bijvoorbeeld beschreven in Bowler & Winter, 1996, Britisch Ceramic Transactions, 95-2, 82-86, of in KNB, 2016, Schoon Metselwerk: Oorzaken en Preventie van Witte Uitslag of nog in Brocken & Nijlen, 2004, 13th Intl. Brick & Block Masonry Conference, Amsterdam. Het doel van deze uitvinding is om te voorzien in een metselmortelsamenstelling voor metselmortel waarmee dit gekende probleem sterk gereduceerd kan worden.A known problem with existing masonry mortars used to build up masonry is the occurrence of late efflorescence, which is persistent and permanent and shows a light, white-grey haze on the surface. Typically for this type of efflorescence, they only appear after a few months or even only after one or two years after completion of the building. The efflorescence mentioned here can consist of hydrated or non-hydrated forms of CaSO4, and possibly also as double salts with other cations such as Na, K or Mg, or in combination with CaCO2. These efflorescences are typically described as late gypsum efflorescence, as described for example in Bowler & Winter, 1996, Britisch Ceramic Transactions, 95-2, 82-86, or in KNB, 2016, Schoon Metselwerk: Causes and Prevention of White Rash or still in Brocken & Nijlen, 2004, 13th Intl. Brick & Block Masonry Conference, Amsterdam. The object of this invention is to provide a masonry mortar composition for masonry mortar with which this known problem can be greatly reduced.
Dit doel van de uitvinding wordt bereikt door te voorzien in een metselmortelsamenstelling voor metselmortel, omvattende tussen 5 en 25 w% anorganisch bindmiddel, waarbij dit bindmiddel bestaat uit calcium aluminaat cement, waarbij dit calcium aluminaat cement omvat: - tussen 30 w% en 80 w% Al,03; - minder dan 0,1 w% CI; - minder dan 0,4 w% alkali; - minder dan 0,3 w% SO:.This object of the invention is achieved by providing a masonry mortar composition for masonry mortar, comprising between 5 and 25 wt.% inorganic binder, this binder consisting of calcium aluminate cement, wherein this calcium aluminate cement comprises: - between 30 wt.% and 80 wt. % Al,03; - less than 0.1 w% CI; - less than 0.4 wt% alkali; - less than 0.3 w% SO2.
De hierbij en hierna gebruikte percentages zijn respectievelijk massapercentages van de totale metselmortel en massapercentages van het totaal aan bindmiddel, die bepaald worden volgens de testmethode conform EN 196-2. Het alkali-gehalte is uitgedrukt als Na20-equivalent (Na:O+0,658 K50).The percentages used here and below are respectively mass percentages of the total masonry mortar and mass percentages of the total binder, which are determined according to the test method in accordance with EN 196-2. The alkali content is expressed as Na2O equivalent (Na:O+0.658 K50).
Met metselmortel met een dergelijke metselmortelsamenstelling wordt het genoemde probleem van late gipsuitbloeiingen sterk gereduceerd. Een gekende versnelde methode om hiertoe deze secundaire gipsuitbloeiingen te meten is beschreven in de thesis van Chwast, 2017, Gypsum eflorescence on clay brick masonry. Ph. D. Thesis, KU Leuven.With masonry mortar with such a masonry mortar composition, the aforementioned problem of late gypsum efflorescence is greatly reduced. A known accelerated method to measure these secondary gypsum efflorescences for this purpose is described in Chwast's thesis, 2017, Gypsum eflorescence on clay brick masonry. Ph. D. Thesis, KU Leuven.
Een dergelijke metselmortel bloeit op zichzelf niet of nauwelijks uit zodat deze bij gebruik in combinatie met gevelstenen een aanzienlijke reductie van het gekende probleem met zich mee brengt. Uitbloeiingen veroorzaakt door de mortel, en die veroorzaakt worden door de interactie van mortel met baksteen kunnen hierbij tegengegaan worden.Such a masonry mortar does not or hardly bleed by itself, so that when used in combination with facing bricks it entails a considerable reduction of the known problem. Efflorescence caused by the mortar and caused by the interaction of mortar with brick can be prevented here.
De metselmortel volgens deze uitvinding is met een breed gamma aan bakstenen met verschillende initiële absorptieklassen (volgens EN 771) te verwerken tot metselwerk.The masonry mortar according to this invention can be processed into masonry with a wide range of bricks with different initial absorption classes (according to EN 771).
Een metselmortel volgens de uitvinding vereist geen bijkomende bewerking of barrière tussen baksteen en mortel, zoals een hydrofuge.A masonry mortar according to the invention does not require any additional processing or barrier between brick and mortar, such as a hydrofuge.
Bij bestaande metselmortels dienen bepaalde bakstenen eerst in een hydrofuge oplossing ondergedompeld te worden om in metselwerk te verwerken om het genoemde probleem tegen te gaan.With existing masonry mortars, certain bricks must first be dipped in a hydrofuge solution to be processed in masonry in order to counteract the problem mentioned.
Met een metselmortel met een metselmortelsamenstelling volgens deze uitvinding is voor een zelfde eindresultaat geen dergelijke bijkomende bewerking van de bakstenen vereist.With a masonry mortar with a masonry mortar composition according to this invention, no such additional processing of the bricks is required for the same end result.
Metselwerk met metselmortel met een metselmortelsamenstelling volgens deze uitvinding blijft zo dezelfde positieve eigenschappen hebben van bestaand metselwerk, waarbij het risico op uitbloeiingen aanzienlijk beperkt is.Masonry with masonry mortar with a masonry mortar composition according to this invention thus continues to have the same positive properties of existing masonry, whereby the risk of efflorescence is considerably limited.
In tegenstelling tot gehydrofobeerde gevelstenen dient hier dus geen aangepaste mortel gebruikt te worden vanwege de verlaagde zuigkracht van de baksteen.In contrast to hydrophobized facing bricks, no adapted mortar should be used here because of the reduced suction power of the brick.
Tijdens in situ testen is gebleken dat deze uitvinding ook het probleem van uitbloeiingen van zouten die ontstaan tijdens of onmiddellijk na de bouwfase, sterk vermindert.In-situ testing has shown that this invention also greatly reduces the problem of salt efflorescence occurring during or immediately after the construction phase.
Deze uitbloeiingen kunnen bestaan uit goed oplosbare zouten, afkomstig van het gevelmetselwerk zelf, en omvatten enkele of combinaties van al dan niet gehydrateerde vormen van Na2SO4, K;SO4 en MgSO4. Ook kalkuitbloeiingen kunnen hieronder vallen.These efflorescences can consist of highly soluble salts, originating from the masonry itself, and include single or combinations of hydrated or non-hydrated forms of Na2SO4, KSO4 and MgSO4. Lime efflorescence can also fall under this.
Aldus kan deze metselmortelsamenstelling bescherming bieden tegen de zogeheten initiële uitbloeiingen, die gebouwen al tijdens de bouwfase kunnen ontsieren.This masonry mortar composition can thus provide protection against the so-called initial efflorescence, which can already disfigure buildings during the construction phase.
De karakteristieke afschuifsterke van metselmortel met een dergelijke metselmortelsamenstelling volgens deze uitvinding ligt boven de gevraagde minimale eis van 0,15 N/mm? volgens EN 1052-3. Afhankelijk van de gebruikte baksteen en zijn initiële waterabsorptieklasse, varieert de karakteristieke afschuifsterkte tussen 0,24 N/mm? en 0,34 N/mm”. De metselmortelsamenstelling draagt bij aan een duurzame, veilige bouwoplossing.The characteristic shear strength of masonry mortar with such a masonry mortar composition according to this invention is above the requested minimum requirement of 0.15 N/mm? according to EN 1052-3. Depending on the brick used and its initial water absorption class, the characteristic shear strength varies between 0.24 N/mm? and 0.34 N/mm”. The masonry mortar composition contributes to a sustainable, safe building solution.
Metselmortel met een dergelijke metselmortelsamenstelling heeft een lagere alkaliniteit en bevat geen chroom in tegenstelling tot traditionele metselmortels.Masonry mortar with such a masonry mortar composition has a lower alkalinity and does not contain chromium in contrast to traditional masonry mortars.
Voorkeurdragend omvat het calcium aluminaat cement van een metselmortelsamenstelling volgens deze uitvinding: - tussen 35 w% en 70 w% Al,03; - minder dan 0,1 w% CI; - minder dan 0,2 w% alkali; - minder dan 0,1 w% SO:. Verder voorkeurdragend omvat een metselmortelsamenstelling bij voorkeur tussen 10% en 20% anorganische bindmiddel.Preferably, the calcium aluminate cement of a masonry mortar composition according to this invention comprises: - between 35 wt.% and 70 wt.% Al,03; - less than 0.1 w% CI; - less than 0.2 wt% alkali; - less than 0.1 w% SO2. Further preferred, a masonry mortar composition preferably comprises between 10% and 20% inorganic binder.
De metselmortelsamenstelling volgens deze uitvinding kan verder meer specifiek tussen 70 w% en 95 w% aggregaat volgens EN 13139 omvatten. Voorkeurdragend omvat de metselmortelsamenstelling tussen 75% en 90% aggregaat.The masonry mortar composition according to this invention may further comprise more specifically between 70 wt% and 95 wt% aggregate according to EN 13139. Preferably, the masonry mortar composition comprises between 75% and 90% aggregate.
Verder voorkeurdragend wordt gewassen kwartszand als aggregaat voorzien om de aanwezigheid van oplosbare alkaliën en sulfaten zoveel mogelijk te beperken. Nog meer voorkeurdragend is dit gewassen kwartszand ook gedroogd.Further preferably, washed quartz sand is provided as aggregate to minimize the presence of soluble alkalis and sulphates. Even more preferably, this washed quartz sand is also dried.
De metselmortelsamenstelling omvat verder bij voorkeur tussen 0 w% en 5 w% organisch bindmiddel. Meer specifiek omvat deze metselmortelsamenstelling bij voorkeur tussen 0,4 w% en 2,5 w% organische bindmiddel. Een dergelijk organisch bindmiddel kan meer specifiek onder de vorm van redispergeerbaar polymeer poeder voorzien worden om de fysische eigenschappen te verbeteren in functie van de gevraagde afschuif-, buigtrek- en druksterkte.The masonry mortar composition further preferably comprises between 0 wt% and 5 wt% organic binder. More specifically, this masonry mortar composition preferably comprises between 0.4 wt% and 2.5 wt% organic binder. More specifically, such an organic binder can be provided in the form of redispersible polymer powder in order to improve the physical properties in function of the required shear, bending tensile and compressive strength.
Daarnaast kan de metselmortelsamenstelling meer specifiek tussen 0 w% en 3 w% additieven omvatten. Bij voorkeur omvat de metselmortelsamenstelling daarbij tussen 0 w% en 2 w% additieven.In addition, the masonry mortar composition may more specifically comprise between 0 wt% and 3 wt% additives. The masonry mortar composition preferably comprises between 0 wt% and 2 wt% additives.
Verder omvat de metselmortelsamenstelling bij voorkeur tussen 0,1% en 0,5% cellulose ether- en derivaten, om de verwerking, afwerking en afbinding te sturen in functie van de laagdikte van de metselmortel, metselmortelsamenstelling, omstandigheden en zuigkracht van de baksteen. Daarnaast kan een metselmortelsamenstelling volgens deze uitvinding ook 5 gebruikelijke vulstoffen (aggregaten) volgens EN 13139 omvatten. Deze metselmortelsamenstelling omvat bij voorkeur minder dan 1 w% alkali en minder dan 0,08 w% oplosbare sulfaten en nog meer voorkeurdragend minder dan 0,1 w% alkali en minder dan 0,02 w% oplosbare sulfaten.Furthermore, the masonry mortar composition preferably comprises between 0.1% and 0.5% cellulose ether and derivatives, in order to control the processing, finishing and binding in function of the layer thickness of the masonry mortar, masonry mortar composition, conditions and absorbency of the brick. In addition, a masonry mortar composition according to this invention can also contain 5 usual fillers (aggregates) according to EN 13139. This masonry mortar composition preferably comprises less than 1 wt% alkali and less than 0.08 wt% soluble sulfates and even more preferably less than 0.1 wt% alkali and less than 0.02 wt% soluble sulphates.
Het doel van deze uitvinding wordt daarnaast ook bereikt door te voorzien in een samenstel van een metselmortel en bakstenen, waarbij de metselmortel een hier boven beschreven metselmortelsamenstelling volgens de uitvinding omvat.In addition, the object of this invention is also achieved by providing an assembly of a masonry mortar and bricks, wherein the masonry mortar comprises a masonry mortar composition according to the invention described above.
De bakstenen van een dergelijke samenstel kunnen daarbij meer specifiek gekenmerkt zijn door een initiële wateropname van minder dan 3 kg/m?.min en een oplosbaar gehalte sulfaten van minder dan 0,01 w% of meer dan 0,1 w%. De initiële wateropname wordt daarbij volgens EN771 bepaald en het w% volgens IC analyse. Metselwerk dat opgetrokken wordt met een dergelijk samenstel zal geen uitbloeiingen vertonen zoals hierboven beschreven.The bricks of such an assembly can be more specifically characterized by an initial water absorption of less than 3 kg/m2.min and a soluble content of sulfates of less than 0.01 wt.% or more than 0.1 wt.%. The initial water absorption is determined according to EN771 and the w% according to IC analysis. Masonry built with such an assembly will not show efflorescence as described above.
Alternatief kunnen de bakstenen van een samenstel volgens deze uitvinding meer specifiek gekenmerkt zijn door een initiële wateropname van meer dan 3 kg/m?.min en een milliequivalentverhouding van het aandeel oplosbaar Ca gehalte ten opzichte van het totaal aandeel kationen van meer dan 0,9 med.Alternatively, the bricks of an assembly according to the invention may be more specifically characterized by an initial water absorption of more than 3 kg/m2.min and a milliequivalent ratio of the proportion of soluble Ca content to the total proportion of cations of more than 0.9 med.
De meq verhouding wordt daarbij gemeten volgens ICP-analyse. Metselwerk opgetrokken met een dergelijk samenstel kan bij de versnelde proef volgens Chwast, 2017 nog enige uitbloeiingen vertonen vanwege het strenge karakter van de versnelde proef, waarbij alle aanwezige zouten uit het mortelsysteem gehaald worden. In de praktijk vertoont een dergelijk samenstel geen tot zeer laag risico op genoemde uitbloeiingen. Uit praktijktesten blijkt dat zelfs de meest risicovolle bakstenen in combinatie met deze metselmortel met een metselmortelsamenstelling volgens deze uitvinding een nagenoeg uitbloeivrij metselwerk kunnen opleveren, mits inachtneming van de verwerkingsinstructies en aandacht voor uitvoering van het metselwerk. Uiteraard kunnen met een metselmortelsamenstelling volgens deze uitvinding zoutuitbloeiingen die afkomstig zijn van externe factoren, niet tegengegaan worden.The meq ratio is thereby measured according to ICP analysis. Brickwork built with such an assembly can still show some efflorescence in the accelerated test according to Chwast, 2017 due to the strict nature of the accelerated test, in which all salts present are removed from the mortar system. In practice, such an assembly shows no to very low risk of said efflorescence. Practical tests have shown that even the most risky bricks in combination with this masonry mortar with a masonry mortar composition according to this invention can produce a virtually efflorescence-free masonry, provided the processing instructions are observed and attention is paid to the execution of the masonry. Naturally, with a masonry mortar composition according to this invention, salt efflorescence originating from external factors cannot be prevented.
Zo zouden CaSO4 of andere zouten, die veroorzaakt worden door het uitspoelen van bijvoorbeeld uithardend beton in de constructie, niet kunnen verhinderd worden van uit te bloeien op de gevel. Bij een samenstel volgens deze uitvinding zullen uitbloeiingen die veroorzaakt kunnen worden door de mortel, de interactie van mortel met baksteen of enkel door de baksteen, tegengegaan worden.For example, CaSO4 or other salts, which are caused by the leaching of, for example, hardening concrete in the construction, cannot be prevented from blooming on the facade. With an assembly according to the invention, efflorescence that can be caused by the mortar, the interaction of mortar with brick or only by the brick will be counteracted.
Het doel van deze uitvinding wordt tenslotte ook bereikt door te voorzien in metselwerk dat opgetrokken wordt met een hier boven beschreven samenstel volgens deze uitvinding.Finally, the object of this invention is also achieved by providing brickwork that is erected with an assembly according to this invention described above.
Deze uitvinding wordt nu nader toegelicht aan de hand van de hierna volgende gedetailleerde beschrijving van een uitvoeringsvorm van een metselmortelsamenstelling en metselwerk volgens deze uitvinding. De bedoeling van deze beschrijving is uitsluitend verduidelijkende voorbeelden te geven en om verdere voordelen en bijzonderheden van de uitvinding aan te duiden, en kan dus niet geïnterpreteerd worden als een beperking van het toepassingsgebied van de uitvinding of van de in de conclusies opgeëiste octrooirechten.This invention will now be further elucidated on the basis of the following detailed description of an embodiment of a masonry mortar composition and masonry according to this invention. The purpose of this description is only to provide illustrative examples and to point out further advantages and features of the invention, and thus should not be construed as limiting the scope of the invention or the patent rights claimed in the claims.
Een droge metselmortel met een metselmortelsamenstelling met 79,08 w% gedroogd kwartszand, 20,00 w% anorganisch bindmiddel, 0,90 w% organisch bindmiddel en 0,02 w% cellulose-ether werd gebruikt.A dry masonry mortar with a masonry mortar composition containing 79.08 wt% dried quartz sand, 20.00 wt% inorganic binder, 0.90 wt% organic binder and 0.02 wt% cellulose ether was used.
Van deze metselmortel werden proefstukken gemaakt voor buigtreksterkte en druksterkte conform NBN EN 1015-11, voor afschuifsterkte conform NBN 1052-3. De afschuifsterkte proefstukken werden gemaakt met 2 soorten bakstenen te weten: bakstenen met een initiële wateropname van 3 kg/m?.min en bakstenen met een initiële wateropname van 1 kg/m?.min.Test pieces were made of this masonry mortar for bending tensile strength and compressive strength in accordance with NBN EN 1015-11, for shear strength in accordance with NBN 1052-3. The shear strength test pieces were made with 2 types of bricks, namely: bricks with an initial water absorption of 3 kg/m?.min and bricks with an initial water absorption of 1 kg/m?.min.
Deze proefstukken werden 28 dagen bewaard conform NBN EN 1015-11 (buigtreksterkte en druksterkte) en conform NBN EN 1052-3 (afschuifsterkte). Op basis van de mortel zijn met de twee baksteensoorten zowel proefmuren gemetseld en proefstukken gemaakt.These test pieces were stored for 28 days in accordance with NBN EN 1015-11 (bending tensile strength and compressive strength) and in accordance with NBN EN 1052-3 (shear strength). Based on the mortar, test walls and test pieces were made with the two types of brick.
De proefmuren (2m x 2,5m) zijn buiten opgesteld in België, dat een matig klimaat heeft met frisse vochtige zomers en zachte regenachtige winters.The test walls (2m x 2.5m) have been set up outside in Belgium, which has a moderate climate with cool humid summers and mild rainy winters.
Het gevelmetselwerk is naar het zuidwesten gericht voor maximale blootstelling aan regen, wind en zon en is verankerd in een snelbouwsteen met spouw van 5cm.The facade masonry faces south-west for maximum exposure to rain, wind and sun and is anchored in a quick-build brick with a 5cm cavity.
Het geheel heeft een overkapping die maximale afwatering op de gevelsteen favoriseert.The whole has a roof that favors maximum drainage on the facing brick.
De proefmuren met de voorgestelde oplossing worden geflankeerd door proefmuren met een CEM I mortelreceptuur die in de zogenaamde ATM test onmiskenbaar late gipsuitbloeiingen vertoonde.The test walls with the proposed solution are flanked by test walls with a CEM I mortar recipe that unmistakably showed late gypsum efflorescence in the so-called ATM test.
Deze laatste worden als referentie genomen teneinde te kunnen waarborgen dat de condities met een andere metselmortel wel late uitbloeiingen veroorzaken.The latter are taken as a reference in order to guarantee that the conditions with another masonry mortar do cause late efflorescence.
De proefstukken zijn onderworpen aan de zogenaamde ATM test zoals beschreven in de eerder genoemde Chwast, 2017. Na twee jaar vertonen de proefmuren met de vooropgestelde metselmortel in voorgenoemde buitencondities geen initiële en late uitbloeiingen, dit in tegenstelling tot de referentie proefmuren.The test pieces have been subjected to the so-called ATM test as described in the aforementioned Chwast, 2017. After two years, the test walls with the proposed masonry mortar in the aforementioned outdoor conditions show no initial and late efflorescence, in contrast to the reference test walls.
Na de versnelde ATM proef vertoont deze proefopstelling waarbij uitgeharde en gecarbonateerde mortel aan het proefsteentje hecht, weinig tot geen uitbloeiingen.After the accelerated ATM test, this test set-up, in which hardened and carbonated mortar adheres to the test stone, shows little or no efflorescence.
Dit wilt zeggen dat minder dan 5% of minder dan 10% van het oppervlak uitbloeiingen vertoont, waarbij dit percentage bepaald werd aan de hand van de ratio bedekte oppervlak met uitbloeiingen ten opzichte van het totale oppervlak van het proefsteentje door middel van fotosoftware.This means that less than 5% or less than 10% of the surface shows efflorescence, where this percentage was determined using the ratio of the surface area covered with efflorescence to the total surface of the test stone by means of photo software.
De uitvinding kan toegepast worden in zowel in situ als in prefab situaties.The invention can be used in both in situ and prefab situations.
Claims (12)