NL1002457C2 - Filler-material production method for heating cushion - involves using fruit kernels which are cleaned and washed before drying at roughly 120 degrees Celsius

Info

Publication number: NL1002457C2
Application number: NL1002457A
Authority: NL
Inventors: Henrica Wil Velzen-Bastiaansen
Original assignee: Velzen Bastiaansen Henrica Wil
Priority date: 1996-02-27
Filing date: 1996-02-27
Publication date: 1998-02-20
Also published as: NL1002457A1

Abstract

The kernels are freed of the fruit flesh and washed in water to remove all the latter together with dirt, before drying at roughly 120 degrees C. Cherrystones can be used as the material, and drying can be for ten minutes in an oven. The temperature gradually rises to 120 degrees, giving the stones a moisture content of 5 to 10 and preferably 7 per cent. Hygroscopic material such as zeolite can be added to the stones, which can be contained in a hose of natural fibre such as cotton.

Description

-1 - WERKWIJZE VOOR HET BEREIDEN VAN VULMATERIAAL VOOR EEN OPLAADBAAR WARMTEKUSSEN, ALSMEDE EEN MET DIT VULMATERIAAL VERVAARDIGD WARMTEKUSSEN.-1 - METHOD FOR PREPARING FILLING MATERIAL FOR A RECHARGEABLE HEAT CUSHION AND A HEAT CUSHION MADE WITH THIS FILLING MATERIAL.

De onderhavige uitvinding heeft betrekking op een werkwijze voor het bereiden 10 van vulmateriaal voor een oplaadbaar warmtekussen, alsmede op een met dit vulmateriaal vervaardigd warmtekussen. In de onderhavige beschrijving wordt onder een oplaadbaar warmtekussen een kussen verstaan, dat bestaat uit een hoes van een geschikt vliesvormig materiaal, bij voorkeur een weefsel van een natuurlijke vezel, zoals katoen, welke hoes is gevuld met een vulmateriaal, dat een relatief grote warmtecapaciteit heeft. Het kussen is 15 bestemd om te worden verwarmd, waarbij het vulmateriaal de warmte zolang mogelijk vasthoudt en geleidelijk weer aan de omgeving afgeeft. Een dergelijk warmtekussen, dat in feite de functie van een conventionele waterkruik vervult, is bestemd om het menselijk lichaam plaatselijk te verwarmen voor het verdrijven van koude en/of als therapeutisch hulpmiddel ter verlichting van pijn of voor het behandelen van stijve spieren, maar kan ook 20 worden gebruikt als warmtebron in bedden en dergelijke.The present invention relates to a method for preparing filling material for a rechargeable heating pad, as well as to a heating pad manufactured with this filling material. In the present description, a rechargeable heating pad is understood to mean a cushion consisting of a cover of a suitable nonwoven material, preferably a fabric of a natural fiber, such as cotton, which cover is filled with a filling material, which has a relatively large heat capacity. . The cushion is intended to be heated, the filling material retaining the heat for as long as possible and gradually releasing it to the environment. Such a heating pad, which in fact fulfills the function of a conventional water bottle, is intended to heat the human body locally for expelling cold and / or as a therapeutic aid for pain relief or for the treatment of stiff muscles, but can also 20 are used as a heat source in beds and the like.

Uit de internationale octrooiaanvrage WO 92/09250 is een flexibel kussen bekend, waarvan het vulmateriaal bestaat uit een synthetisch kneedbaar rubberachtig materiaal, dat is vermengd met een materiaal, dat elektromagnetische straling absorbeert. Een dergelijk kussen heeft een platte dunne vorm en is bedoeld om als een laag op een bepaald gebied 25 van het lichaam te worden aangebracht. Dit kussen kan worden opgewarmd in een huishoudelijke magnetron (microwave). Een dergelijk massief, kneedbaar rubber is echter door het gewicht en de substantie niet geschikt als vulmateriaal voor een kussen.International patent application WO 92/09250 discloses a flexible cushion, the filling material of which consists of a synthetic, malleable rubber-like material, which is mixed with a material that absorbs electromagnetic radiation. Such a pillow has a flat thin shape and is intended to be applied as a layer on a certain area of the body. This pillow can be heated in a household microwave (microwave). However, such a solid, malleable rubber is not suitable as a filling material for a cushion due to its weight and substance.

Het is een oogmerk van de uitvinding een warmtekussen te verschaffen, dat een goedkoop vulmateriaal met een grote warmtecapaciteit en relatief laag soortelijk gewicht 30 bevat en dat in korte tijd door middel van een huishoudelijke magnetron kan worden verwarmd.It is an object of the invention to provide a heating pad which contains an inexpensive filling material with a large heat capacity and relatively low specific gravity and which can be heated in a short time by means of a domestic microwave oven.

1002*57 21002 * 57 2

Een volgend oogmerk van de onderhavige uitvinding is het verschaffen van een warmtekussen, dat is vervaardigd van natuurlijke materialen en zich gemakkelijk aanpast aan de vormen van het menselijk lichaam.A further object of the present invention is to provide a heating pad, which is made of natural materials and adapts easily to the shapes of the human body.

Aan deze oogmerken wordt volgens de uitvinding voldaan door als 5 vulmateriaal de pitten van steenvruchten, en in het bijzonder kersepitten te gebruiken. Deze pitten komen in het algemeen beschikbaar als afval bij vruchtenverwerkende bedrijven. Aan kersepitten wordt hier de voorkeur gegeven, daar deze niet al te groot zijn, en bovendien een gladoppervlak met een bolle vorm hebben. Hierdoor kunnen de pitten gemakkelijk langs elkaar glijden zodat het vulmateriaal zich gemakkelijk kan aanpassen aan 10 zowel de vorm van de hoes als aan die van het menselijk lichaam, waarbij het kussen tevens prettig aanvoelt.These objects are met according to the invention by using the kernels of stone fruit, and in particular cherry kernels, as filling material. These seeds generally become available as waste from fruit processing companies. Cherry seeds are preferred here, as they are not too large, and moreover have a smooth surface with a convex shape. This allows the pips to slide easily together so that the filling material can easily adapt to both the shape of the cover and that of the human body, while the cushion also feels pleasant.

Teneinde te voldoen aan de algemene eisen van hygiëne en duurzaamheid van het vulmateriaal ondergaan de pitten volgens de uitvinding een behandeling, die bestaat uit de volgende stappen: 15 de pitten worden gewassen in roterende trommels onder het toevoeren van water; de pitten worden vervolgens gedurende enige tijd in een oven verhit bij een temperatuur oplopend tot ongeveer 120 °C.In order to meet the general requirements of hygiene and durability of the filler material, the kernels according to the invention undergo a treatment consisting of the following steps: the kernels are washed in rotating drums with the addition of water; the kernels are then heated in an oven at a temperature rising to about 120 ° C for some time.

Deze behandeling verzekert dat er geen vruchtvlees op de pitten achterblijft en er dus geen bacteriegroei kan optreden.This treatment ensures that no pulp remains on the seeds and therefore no bacterial growth can occur.

20 De pitten bestaan uit een houtachtige schil die een kern omgeeft. Na de hierboven aangegeven behandeling te hebben ondergaan hebben de pitten een vochtgehalte van ongeveer 7%. Dit vochtgehalte maakt het mogelijk de pitten in relatief korte tijd te verwarmen door middel van een huishoudelijke magnetron, daar de magnetronstraling bij voorkeur water verwarmt. Het water zal uit de pitten worden gedreven en op relatief 25 koude plaatsen weer condenseren. Het gecondenseerde water zal opnieuw verdampen en elders weer condenseren enz. Dit proces van verdampen en condenseren verloopt relatief snel, zodat na enkele minuten een zakje met pitten van dezelfde temperatuur wordt verkregen dat enigszins klam aanvoelt. Bij intensief gebruik van het warmtekussen zullen de kersepitten uitdrogen. Hierbij is het gevaar aanwezig van zogenaamde “hot-spots”, 30 d w z. de magnetron verhit het zakje met kersepitten niet gelijkmatig, maar er ontstaan plaatselijk aanzienlijke temperatuurverschillen. Dit uitdrogen met het gevaar van “hotspots” kan worden voorkomen door de pitten te benevelen, bijvoorbeeld door middel van 1002457 3 een plantenspuit. De houtachtige schil van de pitten is namelijk in staat weer vocht te absorberen. Ook wordt volgens de uitvinding voorgesteld aan de kersepitten een hygroscopisch materiaal, bij voorkeur met een zeoliet toe te voegen. Het hygroscopische materiaal zal sneller en meer water uit de omgevende lucht absorberen dan de kersepitten, 5 en zodoende bijdragen tot een gelijkmatigere verwarming hiervan in de magnetron.20 The kernels consist of a woody shell that surrounds a core. After undergoing the above-mentioned treatment, the kernels have a moisture content of about 7%. This moisture content makes it possible to heat the seeds in a relatively short time by means of a household microwave, since the microwave radiation preferably heats water. The water will be driven out of the pips and condensate again in relatively cold places. The condensed water will evaporate again and condense elsewhere, etc. This process of evaporation and condensation proceeds relatively quickly, so that after a few minutes a bag of seeds of the same temperature is obtained, which feels slightly clammy. With intensive use of the heating pad, the cherry seeds will dry out. This poses the danger of so-called “hot spots”, 30 ww. The microwave does not heat the bag of cherry seeds evenly, but there are significant temperature differences locally. This drying out with the danger of “hotspots” can be prevented by misting the seeds, for example by means of a plant sprayer. The woody skin of the seeds is able to absorb moisture again. According to the invention it is also proposed to add a hygroscopic material, preferably with a zeolite, to the cherry seeds. The hygroscopic material will absorb water from the surrounding air faster and more than the cherry seeds, thus contributing to its more even heating in the microwave.

In de bijgaande figuren zijn een aantal mogelijke uitvoeringsvormen van het oplaadbare warmtekussen volgens de uitvinding weergegeven.The accompanying figures show a number of possible embodiments of the rechargeable heating pad according to the invention.

Figuur 1 toont een aanzicht van een eerste multifunctionele basisuitvoeringsvorm van het warmtekussen volgens de uitvinding, waarbij een gedeelte van de hoes is 10 weggelaten voor het tonen van het vulmateriaal;Figure 1 shows a view of a first multifunctional basic embodiment of the heating pad according to the invention, with part of the cover omitted for showing the filling material;

Figuur 2 toont een aanzicht van een tweede uitvoeringsvorm, enFigure 2 shows a view of a second embodiment, and

Figuur 3 toont op kleinere schaal een aanzicht van een derde uitvoeringsvorm.Figure 3 shows a view of a third embodiment on a smaller scale.

In figuur 1 is een eerste multifunctionele basisuitvoeringsvorm van het warmtekussen weergegeven, dat in bovenaanzicht een vierkante vorm heeft, met 15 afmetingen van ongeveer 30 x 30 cm. Dit kussen bestaat uit een alzijdig gesloten hoes 1 van een geschikt weefsel, waarin een hoeveelheid vulmateriaal 2 volgens de uitvinding is aangebracht. Dit model is bijzonder geschikt als kruik voor het gehele lichaam, met name rug, buik en voeten. Zoals zichtbaar in de tekening bestaat het kussen uit een hoes van een weefsel van bijvoorkeur een natuurlijke vezel zoals katoen, waarin het uit gereinigde en 20 gedroogde kersepitten bestaande vulmateriaal is aangebracht.Figure 1 shows a first multifunctional basic embodiment of the heating pad, which in square view has a square shape, with dimensions of approximately 30 x 30 cm. This cushion consists of an all-round closed cover 1 of a suitable fabric, in which an amount of filling material 2 according to the invention has been applied. This model is particularly suitable as a jug for the entire body, especially the back, stomach and feet. As can be seen in the drawing, the cushion consists of a cover of a fabric of preferably a natural fiber such as cotton, in which the filling material consisting of cleaned and dried cherry seeds is applied.

De in figuur 2 weergegeven uitvoeringsvorm heeft een langwerpige vorm, en bevat drie door stiknaden 3 gescheiden compartimenten. Dit model is zeer geschikt om bijvoorbeeld om een lichaamsdeel, zoals de nek te worden geslagen.The embodiment shown in figure 2 has an elongated shape, and contains three compartments separated by stitching seams. This model is very suitable, for example, to be wrapped around a body part, such as the neck.

Tenslotte is in figuur 3 een U-vormig model weergegeven, dat goed op de 25 schouders of de nek blijft liggen. Het zal echter duidelijk zijn dat vele andere modellen en uitvoeringen en formaten mogelijk zijn.Finally, figure 3 shows a U-shaped model, which remains well on the shoulders or neck. However, it will be clear that many other models and designs and sizes are possible.

Alhoewel het hier beschreven oplaadbare warmtekussen in het bijzonder bestemd is om door middel van een huishoudelijke magnetron te worden verwarmd, is het natuurlijk ook mogelijk deze op een andere wijze te verwarmen, bijvoorbeeld in een oven. Het 30 gebruik van een magnetron heeft hierbij het voordeel dat het opwarmen in een zeer korte tijd kan geschieden. Behalve voor het verwarmen van delen van het menselijk lichaam kan 1002457 4 het kussen volgens de uitvinding ook worden gebruikt voor het plaatseiijk afkoelen van het menselijk lichaam.Although the rechargeable heating pad described here is in particular intended to be heated by means of a domestic microwave oven, it is of course also possible to heat it in another way, for example in an oven. The use of a microwave hereby has the advantage that heating can take place in a very short time. In addition to heating parts of the human body, the cushion according to the invention can also be used for locally cooling the human body.

Het feit dat de pitten een slechte warmtegeleider zijn maakt deze uitzonderlijk geschikt als vulmateriaal. De slechte warmte-geleidende eigenschappen hebben tot gevolg S dat de warmte heel geleidelijk aan de omgeving wordt afgestaan, of anders gezegd het kussen houdt de warmte gedurende een lange tijd vast. Het warmtekussen zal hierdoor ook na het afgeven van alle warmte niet koud aanvoelen, zoals dit bijvoorbeeld het geval is bij een waterkruik.The fact that the seeds are a poor conductor of heat makes them exceptionally suitable as a filling material. The poor heat-conducting properties result in S that the heat is released very gradually to the environment, or in other words the cushion retains the heat for a long time. The heat pad will therefore not feel cold even after all the heat has been released, as is the case with a water bottle, for example.

Bovendien zijn kersepitten in feite afval bij kersen verwerkende bedrijven en 10 derhalve goedkoop te verkrijgen. Het volgens de onderhavige uitvinding verkregen oplaadbare warmtekussen is zodoende een milieuvriendelijk product, dat volledig is vervaardigd van natuurlijke materialen.Moreover, cherry seeds are in fact waste from cherry processing companies and are therefore cheap to obtain. The rechargeable heat pad obtained according to the present invention is thus an environmentally friendly product, which is made entirely of natural materials.

100?457100? 457

Claims

1. A method of manufacturing filler material for a rechargeable heat pad, characterized in that the raw material used is stone fruit kernels, which are essentially de-pulped, these kernels are washed in water, in order to remove these pits from dirt and any pulp residues; after which the kernels are dried at a temperature of about 120 ° C.

Method according to claim 1, characterized in that cherry seeds are used as the starting material.

3. Process according to claim 1 or 2, characterized in that the seeds are dried in the oven for 10 minutes at a temperature gradually increasing to about 120 ° C, such that the seeds obtain a moisture content of 5 to 10% , preferably from 7%.

Method according to one or more of the preceding claims 1-3, characterized in that a hygroscopic material is added to the dried kernels. 20

Method according to claim 4, characterized in that a zeolite is used as the hygroscopic material.

6. Rechargeable heating pad, comprising a cover of a nonwoven material, preferably a fabric of a natural fiber, such as cotton, which is filled with a filling material prepared according to one or more of the preceding claims. 1002457