MX2019001045A - Lamina de acero y metodo para la produccion de la misma. - Google Patents

Lamina de acero y metodo para la produccion de la misma.

Info

Publication number
MX2019001045A
MX2019001045A MX2019001045A MX2019001045A MX2019001045A MX 2019001045 A MX2019001045 A MX 2019001045A MX 2019001045 A MX2019001045 A MX 2019001045A MX 2019001045 A MX2019001045 A MX 2019001045A MX 2019001045 A MX2019001045 A MX 2019001045A
Authority
MX
Mexico
Prior art keywords
steel sheet
tempered martensite
thin steel
production method
method therefor
Prior art date
Application number
MX2019001045A
Other languages
English (en)
Inventor
Nakagaito Tatsuya
Kohsaka Noriaki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2019001045A publication Critical patent/MX2019001045A/es

Abstract

Se proporcionan una lámina de acero que tiene una tensión de rotura de 900 MPa o superior y excelente soldabilidad, y un método para la producción de la lámina de acero. La lámina de acero se caracteriza por tener una composición específica y una microestructura que contiene, en términos de fracción de área, ferrita de 30% o menos (incluido 0%), martensita revenida de 70% o más (incluido 100%), y el resto distinto de la ferrita y la martensita revenida de 10% o menos (incluido 0%) en total, la martensita revenida tiene un tamaño de grano promedio de la misma que es de 5 µm o menor, la martensita revenida tiene carburos a base de hierro, los cuales tienen tamaños de partícula promedio de 100 nm o menos, precipitados en límites de grano, y la martensita revenida contiene, en términos de concentración atómica, 5% de átomos o más en total de Si y Mn en los límites de grano de la martensita revenida. La lámina de acero se caracteriza además por tener una tensión de rotura de 900 MPa o superior.
MX2019001045A 2016-08-10 2017-08-10 Lamina de acero y metodo para la produccion de la misma. MX2019001045A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016157761 2016-08-10
PCT/JP2017/029035 WO2018030501A1 (ja) 2016-08-10 2017-08-10 薄鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2019001045A true MX2019001045A (es) 2019-04-25

Family

ID=61162311

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2019001045A MX2019001045A (es) 2016-08-10 2017-08-10 Lamina de acero y metodo para la produccion de la misma.

Country Status (7)

Country Link
US (1) US11066716B2 (es)
EP (1) EP3467135B1 (es)
JP (1) JP6296214B1 (es)
KR (1) KR102206448B1 (es)
CN (1) CN109563582B (es)
MX (1) MX2019001045A (es)
WO (1) WO2018030501A1 (es)

Families Citing this family (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US12065711B2 (en) 2018-07-31 2024-08-20 Jfe Steel Corporation High-strength hot rolled steel sheet and method for manufacturing same
CN109576579A (zh) * 2018-11-29 2019-04-05 宝山钢铁股份有限公司 一种具有高扩孔率和较高延伸率的980MPa级冷轧钢板及其制造方法
JP6950835B2 (ja) * 2019-05-16 2021-10-13 Ｊｆｅスチール株式会社 高強度部材、高強度部材の製造方法及び高強度部材用鋼板の製造方法
WO2020262652A1 (ja) * 2019-06-28 2020-12-30 日本製鉄株式会社 鋼板
WO2020262651A1 (ja) * 2019-06-28 2020-12-30 日本製鉄株式会社 鋼板
KR102682666B1 (ko) * 2019-08-06 2024-07-08 제이에프이 스틸 가부시키가이샤 고강도 박강판 및 그의 제조 방법
MX2022009852A (es) * 2020-02-11 2022-08-17 Tata Steel Ijmuiden Bv Acero ductil laminado en caliente de ultra alta resistencia con alta capacidad de bridado, metodo de fabricacion de dicho acero laminado en caliente y uso del mismo.
KR102487306B1 (ko) * 2020-12-21 2023-01-13 현대제철 주식회사 점용접성 및 성형성이 우수한 초고장력 냉연강판, 초고장력 도금강판 및 그 제조방법
KR20240032138A (ko) * 2021-10-12 2024-03-08 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
MX2024010294A (es) * 2022-03-25 2024-09-02 Jfe Steel Corp Union soldada por puntos de resistencia y metodo para producir la misma.
CN115874112B (zh) * 2022-11-02 2024-04-30 包头钢铁（集团）有限责任公司 一种1300兆帕级冷轧马氏体钢的制造方法
CN120530221A (zh) * 2023-01-30 2025-08-22 杰富意钢铁株式会社 钢板、构件和它们的制造方法
JP7632759B2 (ja) * 2023-01-30 2025-02-19 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
JPWO2024195680A1 (es) * 2023-03-20 2024-09-26
WO2024224583A1 (ja) * 2023-04-28 2024-10-31 Ｊｆｅスチール株式会社 亜鉛めっき鋼板、部材及びそれらの製造方法
EP4663785A1 (en) * 2023-04-28 2025-12-17 JFE Steel Corporation Galvanized steel sheet, member, and production methods therefor

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5858199B2 (ja) 1981-05-02 1983-12-23 株式会社 福山織機製作所 畳縫着機用畳床裁断装置
JP4085826B2 (ja) * 2003-01-30 2008-05-14 Ｊｆｅスチール株式会社 伸びおよび伸びフランジ性に優れた二相型高張力鋼板およびその製造方法
WO2008007785A1 (en) * 2006-07-14 2008-01-17 Kabushiki Kaisha Kobe Seiko Sho High-strength steel sheets and processes for production of the same
RU2464338C2 (ru) * 2007-02-23 2012-10-20 Тата Стил Эймейден Б.В. Холоднокатаная и полученная с непрерывным отжигом полоса высокопрочной стали и способ производства упомянутой стали
EP2216422B1 (en) * 2007-11-22 2012-09-12 Kabushiki Kaisha Kobe Seiko Sho High-strength cold-rolled steel sheet
KR101230728B1 (ko) * 2008-03-07 2013-02-07 가부시키가이샤 고베 세이코쇼 냉간 압연 강판
JP4712882B2 (ja) * 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
EP2683839B1 (en) 2011-03-07 2015-04-01 Tata Steel Nederland Technology B.V. Process for producing high strength formable steel and high strength formable steel produced therewith
JP5800098B2 (ja) * 2013-08-02 2015-10-28 Ｊｆｅスチール株式会社 高強度高ヤング率鋼板およびその製造方法
WO2015093043A1 (ja) 2013-12-18 2015-06-25 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板及びその製造方法
JP2015200013A (ja) 2014-03-31 2015-11-12 株式会社神戸製鋼所 延性、伸びフランジ性、および溶接性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板、および高強度合金化溶融亜鉛めっき鋼板
WO2015151428A1 (ja) * 2014-03-31 2015-10-08 Ｊｆｅスチール株式会社 材質均一性に優れた高強度冷延鋼板およびその製造方法
JP5935843B2 (ja) 2014-08-08 2016-06-15 Ｊｆｅスチール株式会社 スポット溶接性に優れた冷延鋼板およびその製造方法
JP6295893B2 (ja) * 2014-08-29 2018-03-20 新日鐵住金株式会社 耐水素脆化特性に優れた超高強度冷延鋼板およびその製造方法

Also Published As

Publication number Publication date
KR102206448B1 (ko) 2021-01-21
CN109563582B (zh) 2021-08-24
JPWO2018030501A1 (ja) 2018-08-09
CN109563582A (zh) 2019-04-02
KR20190022769A (ko) 2019-03-06
US20190271052A1 (en) 2019-09-05
EP3467135A1 (en) 2019-04-10
JP6296214B1 (ja) 2018-03-20
EP3467135B1 (en) 2020-09-23
EP3467135A4 (en) 2019-06-19
WO2018030501A1 (ja) 2018-02-15
US11066716B2 (en) 2021-07-20

Similar Documents

Publication Publication Date Title
MX2019001045A (es) Lamina de acero y metodo para la produccion de la misma.
MX2019001600A (es) Lamina de acero, y metodo de produccion para la misma.
MX2019001794A (es) Lamina de acero laminada en frio de alta resistencia y el metodo para su produccion.
MX2019001828A (es) Lamina de acero y metodo para la fabricacion de la misma.
MX2018007579A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2020006342A (es) Hoja de acero de alta resistencia y alta formabilidad y metodo de fabricacion.
MX2021004419A (es) Lamina de acero electrogalvanizada de alta resistencia y alto limite de alargamiento y metodo para la fabricacion de la misma.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2017009616A (es) Material de varilla para componentes de maquinas sin revenir, varillas de acero para componentes de maquinas sin revenir y componentes de maquinas sin revenir.
MX2017015333A (es) Lamina de acero rolada en frio de alta resistencia, lamina de acero recubierta de alta resistencia, metodo para fabricar lamina de acero rolada en frio de alta resistencia, y metodo para fabricar lamina de acero recubierta de alta resistencia.
MX2017001689A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2016006777A (es) Componente de lamina de acero formada en caliente y metodo para producir el mismo asi como la lamina de acero para formacion en caliente.
MX2017008295A (es) Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas.
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
MX352397B (es) Lamina de acero de alta resistencia y lamina de acero galvanizada de alta resistencia excelentes en moldeabilidad y metodos de produccion de las mismas.
MX2020006773A (es) Chapa de acero laminada en frio de alta resistencia y metodo para fabricar la misma.
MX2017003993A (es) Lamina de acero laminado en frio de alta resistencia y alta formabilidad o banda de acero y metodo para fabricar la misma.
GB201210376D0 (en) High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
MX2010008404A (es) Chapa de acero de alta resistencia y metodo para elaboracion de la misma.
MX360965B (es) Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma.
MY174534A (en) Steel sheet hot-dip coated with zn-al-mg-based system having excellent workability and method for manufacturing same
MX2017009200A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2017001720A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX361834B (es) Lamina de acero y el metodo para la fabricacion de lamina de acero.