MX2018014324A - Hoja de acero laminada en frio y templada, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo. - Google Patents

Hoja de acero laminada en frio y templada, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo.

Info

Publication number
MX2018014324A
MX2018014324A MX2018014324A MX2018014324A MX2018014324A MX 2018014324 A MX2018014324 A MX 2018014324A MX 2018014324 A MX2018014324 A MX 2018014324A MX 2018014324 A MX2018014324 A MX 2018014324A MX 2018014324 A MX2018014324 A MX 2018014324A
Authority
MX
Mexico
Prior art keywords
cold rolled
vehicle parts
steel sheet
production
average
Prior art date
Application number
MX2018014324A
Other languages
English (en)
Inventor
Soler Michel
Alberto Zuazo Rodriguez Ian
De Diego Calderon Irène
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2018014324A publication Critical patent/MX2018014324A/es

Abstract

La invención trata sobre una hoja de acero laminada en frío y templada que comprende en peso: 0.6 < C < 1.3%, 15.0 = Mn < 35%, 6.0 = Al < 15%, Si = 2.40%, S = 0.015%, P = 0.1%, N = 0.1%, posiblemente uno o más elementos opcionales elegidos entre Ni, Cr y Cu en una cantidad individual de hasta 3% y posiblemente uno o más elementos elegidos entre B, Ta, Zr, Nb, V, Ti, Mo y W en una cantidad acumulada de hasta 2.0%, el resto de la composición se forma de hierro e impurezas inevitables que resultan de la elaboración, la microestructura de dicha hoja que comprende al menos 0.1% de carburos kappa intragranulares, en donde al menos 80% de tales carburos kappa tienen un tamaño promedio por debajo de 30 nm, opcionalmente hasta 10% de ferrita granular, siendo el resto austenita, el tamaño de grano promedio y proporción de aspecto promedio de la austenita es respectivamente 6 µm y comprendida entre 1.5 y 6 y el tamaño de grano promedio y proporción de aspecto de grano promedio de la ferrita, cuando está presente, es respectivamente por debajo de 5 µm y por debajo de 3.0. También trata sobre un método de fabricación y el uso de tal grado para hacer partes de vehículos.
MX2018014324A 2016-05-24 2017-05-23 Hoja de acero laminada en frio y templada, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo. MX2018014324A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2016/000701 WO2017203315A1 (en) 2016-05-24 2016-05-24 Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
PCT/IB2017/000616 WO2017203346A1 (en) 2016-05-24 2017-05-23 Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts

Publications (1)

Publication Number Publication Date
MX2018014324A true MX2018014324A (es) 2019-02-25

Family

ID=56137462

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2018014324A MX2018014324A (es) 2016-05-24 2017-05-23 Hoja de acero laminada en frio y templada, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo.

Country Status (16)

Country Link
US (1) US11486017B2 (es)
EP (1) EP3464665B1 (es)
JP (1) JP6854833B2 (es)
KR (1) KR102246750B1 (es)
CN (1) CN109154049B (es)
BR (1) BR112018071442B1 (es)
CA (1) CA3025444C (es)
ES (1) ES2908407T3 (es)
HU (1) HUE057442T2 (es)
MA (1) MA45131B1 (es)
MX (1) MX2018014324A (es)
PL (1) PL3464665T3 (es)
RU (1) RU2704983C1 (es)
UA (1) UA121623C2 (es)
WO (2) WO2017203315A1 (es)
ZA (1) ZA201806715B (es)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019122960A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts
WO2020115526A1 (en) * 2018-12-04 2020-06-11 Arcelormittal Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
CN114761583B (zh) * 2019-12-13 2024-04-05 安赛乐米塔尔公司 经热处理的冷轧钢板及其制造方法
CN111270158B (zh) * 2020-03-13 2021-03-23 燕山大学 一种低密度耐腐蚀钢及其制备方法和应用
CN111235484B (zh) * 2020-03-13 2021-05-14 燕山大学 一种高强高硬低密度钢及其制备方法和应用
CN111647818B (zh) * 2020-07-02 2021-11-05 武汉科技大学 一种超细晶粒尺寸薄规格高锰高铝钢及生产方法
CN112030077A (zh) * 2020-09-08 2020-12-04 燕山大学 一种含锰高强低密度钢及其制备方法和应用
CN112795836A (zh) * 2020-12-29 2021-05-14 武汉科技大学 一种钛处理降低低密度钢中氮化铝夹杂物的方法
CN114231851B (zh) * 2021-12-22 2023-09-22 广东省科学院新材料研究所 一种纳米碳化物增强耐磨钢及其制备方法和应用
CN114752864B (zh) * 2022-04-25 2022-10-04 燕山大学 一种低密度超高强度高塑性钢及其制备方法和应用
CN114622074B (zh) * 2022-05-12 2022-08-05 中北大学 一种奥氏体不锈钢及其热处理工艺和热处理工艺的用途
CN116695004A (zh) * 2023-04-14 2023-09-05 常州亿富泰特钢有限公司 一种高韧性耐磨高锰钢材料及其制备方法
CN117070859A (zh) * 2023-08-23 2023-11-17 广东省科学院新材料研究所 一种基于氧化膜改性的耐热锰钢及其制备方法和应用
CN120230965B (zh) * 2025-05-30 2025-08-01 江苏沙钢钢铁有限公司 输氢管线用钢及其生产方法

Family Cites Families (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3963531A (en) 1975-02-28 1976-06-15 Armco Steel Corporation Cold rolled, ductile, high strength steel strip and sheet and method therefor
ATE289229T1 (de) 1999-08-06 2005-03-15 Muhr & Bender Kg Verfahren zum flexiblen walzen eines metallbandes
DE10128544C2 (de) 2001-06-13 2003-06-05 Thyssenkrupp Stahl Ag Höherfestes, kaltumformbares Stahlblech, Verfahren zu seiner Herstellung und Verwendung eines solchen Blechs
DE10259230B4 (de) 2002-12-17 2005-04-14 Thyssenkrupp Stahl Ag Verfahren zum Herstellen eines Stahlprodukts
FR2857980B1 (fr) * 2003-07-22 2006-01-13 Usinor Procede de fabrication de toles d'acier austenitique fer-carbone-manganese, a haute resistance, excellente tenacite et aptitude a la mise en forme a froid, et toles ainsi produites
JP4084733B2 (ja) * 2003-10-14 2008-04-30 新日本製鐵株式会社 延性に優れた高強度低比重鋼板およびその製造方法
DE102004037206A1 (de) 2004-07-30 2006-03-23 Muhr Und Bender Kg Fahrzeugkarosserie
FR2876711B1 (fr) 2004-10-20 2006-12-08 Usinor Sa Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese
JP4324072B2 (ja) * 2004-10-21 2009-09-02 新日本製鐵株式会社 延性に優れた軽量高強度鋼とその製造方法
US20090010793A1 (en) * 2004-11-03 2009-01-08 Thyssenkrupp Steel Ag Method For Producing High Strength Steel Strips or Sheets With Twip Properties, Method For Producing a Component and High-Strength Steel Strip or Sheet
FR2878257B1 (fr) 2004-11-24 2007-01-12 Usinor Sa Procede de fabrication de toles d'acier austenitique, fer-carbone-manganese a tres hautes caracteristiques de resistance et d'allongement, et excellente homogeneite
JP4464811B2 (ja) 2004-12-22 2010-05-19 新日本製鐵株式会社 延性に優れた高強度低比重鋼板の製造方法
US20090165897A1 (en) 2005-02-02 2009-07-02 Corus Staal Bv Austenitic steel having high strength and formability, method of producing said steel and use thereof
DE102005008410B3 (de) 2005-02-24 2006-02-16 Thyssenkrupp Stahl Ag Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband
KR100742833B1 (ko) 2005-12-24 2007-07-25 주식회사 포스코 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법
EP1878811A1 (en) 2006-07-11 2008-01-16 ARCELOR France Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced
EP2048256B1 (en) 2006-07-28 2021-11-10 Nippon Steel Corporation Stainless steel sheet for parts and process for manufacturing the same
KR100928795B1 (ko) 2007-08-23 2009-11-25 주식회사 포스코 가공성 및 강도가 우수한 고망간 용융아연도금 강판 및 그제조 방법
KR20090070509A (ko) 2007-12-27 2009-07-01 주식회사 포스코 고연성 및 고강도를 가지는 고망간 도금강판 및 그제조방법
KR100985286B1 (ko) 2007-12-28 2010-10-04 주식회사 포스코 내지연파괴 특성이 우수한 고강도 고망간강 및 제조방법
KR101113666B1 (ko) 2008-08-13 2012-02-14 기아자동차주식회사 초고강도 트윕 강판 및 그 제조방법
DE102008056844A1 (de) 2008-11-12 2010-06-02 Voestalpine Stahl Gmbh Manganstahlband und Verfahren zur Herstellung desselben
EP2208803A1 (de) 2009-01-06 2010-07-21 ThyssenKrupp Steel Europe AG Höherfester, kaltumformbarer Stahl, Stahlflachprodukt, Verfahren zur Herstellung eines Stahlflachprodukts sowie Verwendung eines Stahlflachproduktes
WO2011154153A1 (en) * 2010-06-10 2011-12-15 Tata Steel Ijmuiden Bv Method of producing an austenitic steel
EP2402472B2 (de) 2010-07-02 2017-11-15 ThyssenKrupp Steel Europe AG Höherfester, kaltumformbarer Stahl und aus einem solchen Stahl bestehendes Stahlflachprodukt
WO2012052626A1 (fr) * 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
DE102011117135A1 (de) 2010-11-26 2012-05-31 Salzgitter Flachstahl Gmbh Energie speicherndes Behältnis aus Leichtbaustahl
KR20120065464A (ko) 2010-12-13 2012-06-21 주식회사 포스코 항복비 및 연성이 우수한 오스테나이트계 경량 고강도 강판 및 그의 제조방법
DE102011000089A1 (de) 2011-01-11 2012-07-12 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines warmgewalzten Stahlflachprodukts
DE102011051731B4 (de) 2011-07-11 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts
UA109963C2 (uk) 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
TWI445832B (en) * 2011-09-29 2014-07-21 The composition design and processing methods of high strength, high ductility, and high corrosion resistance alloys
US20150211088A1 (en) 2011-12-23 2015-07-30 Posco Non-magnetic high manganese steel sheet with high strength and manufacturing method thereof
WO2013178887A1 (fr) * 2012-05-31 2013-12-05 Arcelormittal Investigación Desarrollo Sl Acier laminé a chaud ou a froid a faible densite, son procede de mise en oeuvre et son utilisation
JP6374864B2 (ja) 2012-06-05 2018-08-15 ティッセンクルップ スチール ヨーロッパ アーゲーＴｈｙｓｓｅｎｋｒｕｐｐ Ｓｔｅｅｌ Ｅｕｒｏｐｅ Ａｇ 鋼、平鋼材及び平鋼材の製造方法
CN102751363B (zh) 2012-07-05 2015-01-21 友达光电股份有限公司 光伏装置
KR101439613B1 (ko) 2012-07-23 2014-09-11 주식회사 포스코 굽힘 가공성과 연신율이 우수한 고강도 고망간 강판 및 그 제조방법
DE102012110972B3 (de) 2012-11-14 2014-03-06 Muhr Und Bender Kg Verfahren zum Herstellen eines Erzeugnisses aus flexibel gewalztem Bandmaterial und Erzeugnis aus flexibel gewalztem Bandmaterial
JP6055343B2 (ja) 2013-03-13 2016-12-27 株式会社神戸製鋼所 低温曲げ加工性に優れた非磁性鋼およびその製造方法
EP3255170B1 (en) 2013-08-14 2021-03-31 Posco Ultrahigh-strength steel sheet and manufacturing method therefor
US10626476B2 (en) 2013-12-26 2020-04-21 Posco High specific strength steel sheet and method for manufacturing same
CN103820735B (zh) * 2014-02-27 2016-08-24 北京交通大学 一种超高强度C-Al-Mn-Si系低密度钢及其制备方法
KR20180121891A (ko) * 2016-03-01 2018-11-09 타타 스틸 네덜란드 테크날러지 베.뷔. 높은 연성을 가진 저밀도 고강도 오스테나이트 강 스트립 또는 시트, 강의 제조 방법 및 그것의 용도

Also Published As

Publication number Publication date
RU2704983C1 (ru) 2019-11-01
CA3025444A1 (en) 2017-11-30
PL3464665T3 (pl) 2022-03-28
KR20180132930A (ko) 2018-12-12
CN109154049B (zh) 2021-08-03
CA3025444C (en) 2022-04-19
MA45131A (fr) 2019-04-10
US20190276909A1 (en) 2019-09-12
BR112018071442B1 (pt) 2022-12-06
UA121623C2 (uk) 2020-06-25
CN109154049A (zh) 2019-01-04
ZA201806715B (en) 2019-06-26
EP3464665A1 (en) 2019-04-10
EP3464665B1 (en) 2022-02-09
ES2908407T3 (es) 2022-04-29
HUE057442T2 (hu) 2022-05-28
JP6854833B2 (ja) 2021-04-07
WO2017203315A1 (en) 2017-11-30
KR102246750B1 (ko) 2021-04-30
BR112018071442A2 (pt) 2019-02-05
US11486017B2 (en) 2022-11-01
WO2017203346A1 (en) 2017-11-30
JP2019522723A (ja) 2019-08-15
MA45131B1 (fr) 2022-02-28

Similar Documents

Publication Publication Date Title
MX2018014324A (es) Hoja de acero laminada en frio y templada, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo.
CA3025456C (en) Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
MX2018014318A (es) Lamina de acero laminada en frio y recocida, metodo para su produccion y uso de dicho acero para producir partes de vehiculo.
MX2021006508A (es) Lamina de acero recocida y laminada en frio, metodo de produccion de la misma y uso de tal acero para producir piezas de vehiculos.
MX388381B (es) Acero de elevada resistencia y procedimiento de fabricacion.
UA99827C2 (ru) Сталь низкой плотности с хорошей способностью к штамповке, стальной лист, способ его изготовления и применения
PH12019501270A1 (en) HIGH-Mn STEEL PLATE AND MANUFACTURING METHOD THEREFOR
UA99127C2 (ru) Стальная деталь, охлажденная выдержкой в оборудовании, сварное изделие с использованием этой детали, ее изготовление с предварительным покрытием и без него и применение указанной стальной детали
MX348365B (es) Placa de acero o lamina de acero resistente a la abrasion excelente en resistencia al agrietamiento por corrosion y esfuerzo y metodo para la fabricacion de la misma.
UA90873C2 (ru) лист (варианты) и способ производства листа из аустенитной железо-углеродИСТО-марганцовистой стали (варианты)
MX2013011155A (es) Placa de acero o lamina de acero resistente a la abrasion excelente en resistencia al agrietamiento por corrosion y esfuerzo y metodo para la fabricacion de la misma.
CA3077926A1 (en) Steel structure for hydrogen gas with excellent hydrogen embrittlement resistance in high pressure hydrogen gas and method of producing the same
UA112771C2 (uk) Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
UA109963C2 (uk) Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
UA84377C2 (ru) Лист из марганцевой стали аустенитной структуры с высоким сопротивлением замедленному трещинообразованию и способ его изготовления
MX2018009402A (es) Chapa de acero inoxidable ferritico que contiene nb laminada en caliente y metodo para producir la misma, y chapa de acero inoxidable ferritico que contiene nb laminada en frio y metodo para producir la misma.
MX346491B (es) Placa de acero laminada en caliente o en frio, su proceso de fabricacion y su uso en la industria automotriz.
MX2020006334A (es) Seccion de acero que tiene un espesor de al menos 100 mm y el metodo de fabricacion del mismo.
MX2017016905A (es) Acero resistente a la corrosion, metodo para producir dicho acero y uso del mismo.
UA103888C2 (ru) СПОСОБ ПОЛУЧЕНИЯ РАСПЛАВА СТАЛИ С содержанием марганца до 30 МАС. %
MX376541B (es) Hoja de acero laminada en caliente y método de fabricación relacionado.
MX2017004258A (es) Material de acero de alta resistencia para pozos de petróleo y productos tubulares para la industria del petróleo.
MX2020006341A (es) Hoja de acero laminada en frio y tratada termicamente, metodo de produccion de la misma y uso de tal acero para producir partes de vehiculo.
MX2018004385A (es) Acero, producto creado a partir de tal acero, y metodo de fabricacion del mismo.
CA3139633A1 (en) A cold rolled martensitic steel and a method of martensitic steel thereof