Failure analysis and welding repair for water wall connection tube burst of SA210C steelZheng et al., 2014
- Document ID
- 16944036993232705998
- Author
- Zheng X
- Wu N
- Jiang Y
- Li W
- Hao X
- Ke H
- Li W
- Dai X
- Publication year
- Publication venue
- Advanced Materials Research
External Links
Snippet
Through methods, such as microscope analysis, mechanical analysis, chemical analysis, metallography examination etc, the causes resulting in water wall tube bursting of 300MW station boiler have been analyzed. The raw material defects is the primarily inducement of …
- 238000003466 welding 0 title abstract description 53
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CN102756235B (en) | Field welding repair method especially for larger and penetrating defects in steel casting with heavy wall thickness | |
| JP6730927B2 (en) | Products for welded joints with step design | |
| Kumar et al. | An overview of welding aspects and challenges during manufacture of Intermediate Heat Exchangers for 500MWe Prototype Fast Breeder Reactor | |
| Aranđelović et al. | Reparation, inspection and damage analysis of steam boiler | |
| Ma et al. | Failure analysis on circulating water pump of duplex stainless steel in 1000 MW ultra-supercritical thermal power unit | |
| Urzynicok et al. | Application of new GMAW welding methods used in prefabrication of P92 (X10CrWMoVNb9-2) pipe butt welds | |
| Prasanna et al. | Investigation of welding of dissimilar high thickness SA106 Gr. C carbon steel and SA335P12 alloy steel to eradicate the failure in boiler components fabricated through SAW and SMAW processes | |
| CN105127557B (en) | The medicine core gas shielded arc welding Rework Technics of marine engineering large thick steel plate under low temperature environment | |
| Baek et al. | Influence of welding processes and weld configurationon fatigue failure of natural gas branch pipe | |
| Zheng et al. | Failure analysis and welding repair for water wall connection tube burst of SA210C steel | |
| Nascimento et al. | Effects of several TIG weld repairs on the axial fatigue strength of AISI 4130 aeronautical steel‐welded joints | |
| Zheng et al. | Failure Analysis and Welding Repair for Water Wall Tube Burst of 600MW Station Boiler | |
| Zheng et al. | Failure Analysis and Welding Repair for Water Wall Tube Crack of Supercritical Boiler | |
| Zheng et al. | Research on welding repair for reheating hot pipe elbow of 325MW station boiler | |
| Zheng et al. | Failure analysis and welding repair for reheater tube crack of 12Cr1MoV steel | |
| Niu et al. | Research on welding repair for tee joint crack of final superheater header of 300MW station boiler | |
| Wang et al. | Research On Welding Repair For Tee Joint Crack Of Subcritical Power Station Boiler Platen Superheater Header | |
| Sekyi-Ansah et al. | Investigations of weldment joints of exhaust pipes using non-destructive testing (NDT) | |
| Odanović | Some advanced welding technologies applied for repair welding in power plants | |
| Zhao et al. | Effect of repair welding on the creep behavior of a 12cr1mov/gtr-2cm/p91 dissimilar joint | |
| Moradi et al. | Investigation of residual stresses on post weld heat treated A106-GRB steel pipe by holedrilling and FEM | |
| RU2532577C2 (en) | Elimination of metal structure damages | |
| Innogy | " Cold" Weld Repairs using Flux Cored Arc Welding (FCAW) | |
| Abdulsalam | Mechanical Properties of welded steel pipes type 213 Gr T5 used in heat exchangers | |
| Yang et al. | Welding Numerical Simulation Analysis of AP 1000 Insert Plate and Penetration Sleeves Based on ABAQUS |