An investigation on the performance of an imidazoline based commercial corrosion inhibitor on CO2 corrosion of mild steelKhavasfar et al., 2007
View PDF- Document ID
- 13743078308698106563
- Author
- Khavasfar A
- Moayed M
- Jafari A
- Publication year
External Links
Snippet
The performance of an Imidazoline based commercial CORROSION INHIBITOR on CO2 CORROSION of mild steel was investigated in a Cl-containing solution employing LINEAR POLARIZATION RESISTANCE (LPR), POTENTIODYNAMIC POLARIZATION and monitoring …
- 230000002401 inhibitory effect 0 title abstract description 96
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
- C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
- C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
- C23F11/14—Nitrogen-containing compounds
- C23F11/144—Aminocarboxylic acids
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; MISCELLANEOUS COMPOSITIONS; MISCELLANEOUS APPLICATIONS OF MATERIALS
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K8/00—Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations
- C09K8/54—Compositions for in situ inhibition of corrosion in boreholes or wells
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Wei et al. | Corrosion of low alloy steel and stainless steel in supercritical CO2/H2O/H2S systems | |
| Shamsa et al. | Impact of corrosion products on performance of imidazoline corrosion inhibitor on X65 carbon steel in CO2 environments | |
| Lopez et al. | The influence of microstructure and chemical composition of carbon and low alloy steels in CO2 corrosion. A state-of-the-art appraisal | |
| Schmitt | Fundamental aspects of CO2 metal loss corrosion. Part II: Influence of different parameters on CO2 corrosion mechanism | |
| Zhu et al. | Role of bicarbonate in CO2 corrosion of carbon steel | |
| Pfennig et al. | Effect of CO2 and pressure on the stability of steels with different amounts of chromium in saline water | |
| Benamor et al. | Effect of temperature and fluid speed on the corrosion behavior of carbon steel pipeline in Qatari oilfield produced water | |
| Gulbrandsen et al. | Solution chemistry effects on corrosion of carbon steels in presence of CO2 and acetic acid | |
| Quraishi et al. | Inhibition of mild steel corrosion in sulfuric acid solution by thiadiazoles | |
| Esmaeely et al. | Localized corrosion of mild steel in marginally sour environments | |
| Zhao et al. | A comparative study on the corrosion behaviors of X100 steel in simulated oilfield brines under the static and dynamic conditions | |
| Skilbred et al. | Hydrogen uptake during active CO2-H2S corrosion of carbon steel wires in simulated annulus fluid | |
| Gulbrandsen et al. | Effect of oxygen contamination on inhibition studies in carbon dioxide corrosion | |
| Khavasfar et al. | An investigation on the performance of an imidazoline based commercial corrosion inhibitor on CO2 corrosion of mild steel | |
| Li et al. | Corrosion behavior about tubing steel in environment with high H2S and CO2 content | |
| Al-Uqaily | Corrosion inhibition of steel in HCL media using 2-methoxymethyl-benzlamine | |
| Campos et al. | Corrosion of armor wire steel in the annulus of flexible pipes at near neutral pH | |
| Zhao et al. | Effect of chloride concentration on stress corrosion behavior and mechanism of SA516Gr70N steel in alkaline NaCl/Na2S solution | |
| Martin | Inhibition of hydrogen permeation in steels corroding in sour fluids | |
| Akbar et al. | The influence of flow rate, sand and inhibitor on iron carbonate scales under erosion-corrosion conditions using a submerged impingement jet | |
| Cabrini et al. | Corrosion behavior of carbon steels in CCTS environment | |
| Ayyagari et al. | Effect of Acetic Acid on Corrosion Product Layer Formation in Aqueous CO2 Environments | |
| Wang et al. | EffEcts of WElding HEat input on MicrostructurE and corrosion cHaractErization in cgHaz of X80 pipElinE stEEl | |
| Dong et al. | Determination of critical salinity of pitting and uniform corrosion of X60 under CO2-O2 coexistence environment | |
| Deng et al. | Effect of microstructure on corrosion of welded joints of X80 steel in water saturated supercritical CO2 |