Cyclic pressure testing of full-scale pipes to evaluate fatigue damage to girth welds containing welding defects

Yan et al., 2025

View PDF
Document ID
12554666378995365312
Author
Yan B
Feng Q
Zhang Y
Chen J
Fu L
Publication year
Publication venue
Engineering Failure Analysis

External Links

Snippet

Onshore pipelines can be subject to fatigue damage due to internal pressure fluctuation, thermal loads or mechanical loads. Welding defects were detected in two girth welds during an in-line inspection and were confirmed in the inspection after excavation. They were either …
Continue reading at papers.ssrn.com (PDF) (other versions)

Classifications

    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0058—Kind of property studied
    • G01N2203/006—Crack, flaws, fracture or rupture
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/02—Indexing codes associated with the analysed material
    • G01N2291/028—Material parameters
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N29/00—Investigating or analysing materials by the use of ultrasonic, sonic or infrasonic waves; Visualisation of the interior of objects by transmitting ultrasonic or sonic waves through the object
    • G01N29/04—Analysing solids
    • G01N29/06—Visualisation of the interior, e.g. acoustic microscopy
    • G01N29/0654—Imaging
    • G01N29/069—Defect imaging, localisation and sizing using, e.g. time of flight diffraction [TOFD], synthetic aperture focusing technique [SAFT], Amplituden-Laufzeit-Ortskurven [ALOK] technique
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/26—Scanned objects
    • G01N2291/263—Surfaces
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/26—Scanned objects
    • G01N2291/267—Welds
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N29/00—Investigating or analysing materials by the use of ultrasonic, sonic or infrasonic waves; Visualisation of the interior of objects by transmitting ultrasonic or sonic waves through the object
    • G01N29/22—Details, e.g. general constructional or apparatus details
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N3/08—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N27/00—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means
    • G01N27/72—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables
    • G01N27/82—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables for investigating the presence of flaws
    • G01N27/83—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables for investigating the presence of flaws by investigating stray magnetic fields
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/10—Number of transducers
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/04—Wave modes and trajectories
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0014—Type of force applied

Similar Documents

Publication Publication Date Title
Benjamin et al. Burst tests on pipeline containing interacting corrosion defects
Zhang et al. Investigation of the tensile strain response of the girth weld of high-strength steel pipeline
Zhao et al. Elastic-plastic fracture analyses for misaligned clad pipeline containing a canoe shape surface crack subjected to large plastic deformation
Yan et al. Cyclic pressure testing of full-scale pipes to evaluate fatigue damage to girth welds containing welding defects
Fairchild et al. Full-Scale pipe strain test quality and safety factor determination for strain-based engineering critical assessment
Yang et al. Full-scale experimental investigation of the fracture behaviours of welding joints of APL X80 wide plate based on DIC technology
Wang et al. Tensile strain limits of buried defects in pipeline girth welds
Wang et al. Effect of strain aging on mechanical properties and engineering critical assessment of X80 girth weld metal
Verstraete et al. Pressure correction factor for strain capacity predictions based on Curved Wide Plate testing
Xu et al. Simulation of fatigue properties for the weld joint of the X80 weld pipe before and after removing the weld reinforcement
Krishnan et al. Evaluation of fracture resistance of AISI type 316LN stainless steel base and welded pipes with circumferential through-wall crack
Zangeneh et al. Fitness-for-Service assessment of a Hydrogen-Induced crack in an inlet gas separator pressure vessel using computational modelling
Chong et al. Effects of elevated temperatures on the mechanical properties of nickel-based alloy clad pipelines girth welds
Lei et al. Full-scale burst test and finite element simulation of 32 inch oil pipe with girth weld defects
Wang et al. Integrity management of ground movement hazards
Lukács et al. Full-scale Fatigue and Burst Tests on Notched Pipeline Girth Welds, under Complex Loading Conditions
Carlucci et al. Crack initiation and growth in bimetallic girth welds
Jia et al. Material Properties and Flaw Characteristics of Vintage Girth Welds
Fairchild et al. Full-Scale Testing for Strain-Based Design Pipelines: Lessons Learned and Recommendations
Boot et al. In-situ hollow sample setup design for mechanical characterisation of gaseous hydrogen embrittlement of pipeline steels and welds. Metals 2021, 11, 1242
Lu et al. A Case Study of Predicting Tensile Strain Capacity of In-Service Pipelines
Zhu et al. Tensile properties of welded joints with delayed hydride crack
Kalyanam et al. Mode mixity in the fracture toughness characterization of HAZ material using SEN (T) testing
Chong et al. Engineering Critical Assessment of nickel-based clad pipeline girth welds in a wet H2S-containing environment
Fairchild et al. Observations on the design, execution, and use of full-scale testing for strain-based design pipelines