Chen et al., 2022 - Google Patents

Polymer Brush Induced Electroless Copper Plating on PA12 Surface for Tensile Strength Enhancement of Selective Laser Sintering Part

Chen et al., 2022

Document ID
11679855640535412797
Author
Chen Z
Gui C
Yao W
Li P
Publication year
Publication venue
Journal of Materials Engineering and Performance

External Links

Snippet

Metal particles can be deposited on nylon 12 (PA12) surface with excellent metal/substrate interface and distribution by electroless plating (EP), but the use of noble metal as EP catalyst would enhance the cost of raw materials and restrict its application. In this work, we …
Continue reading at link.springer.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1646—Characteristics of the product obtained
    • C23C18/165—Multilayered product
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/31—Coating with metals
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/18—Pre-treatment of the material to be coated
    • C23C18/20—Pre-treatment of the material to be coated of organic surfaces, e.g. resins
    • C23C18/2006—Pre-treatment of the material to be coated of organic surfaces, e.g. resins by other methods than those of C23C18/22 - C23C18/30
    • C23C18/2046—Pre-treatment of the material to be coated of organic surfaces, e.g. resins by other methods than those of C23C18/22 - C23C18/30 by chemical pretreatment

Similar Documents

Publication Publication Date Title
Dharmadasa et al. Room temperature synthesis of a copper ink for the intense pulsed light sintering of conductive copper films
Garcia et al. ABS polymer electroless plating through a one-step poly (acrylic acid) covalent grafting
Hua et al. Preparation and characterization of nickel-coated carbon fibers by electroplating
Zhang et al. Selective metallization induced by laser activation: fabricating metallized patterns on polymer via metal oxide composite
Chen et al. Layer by layer electroless deposition: an efficient route for preparing adhesion-enhanced metallic coatings on plastic surfaces
Singh et al. Effect of hybrid reinforcements on the mechanical properties of copper nanocomposites
Huang et al. Surface metallization of PET sheet: Fabrication of Pd nanoparticle/polymer brush to catalyze electroless nickel plating
Chen et al. Formation of reflective and conductive silver film on ABS surface via covalent grafting and solution spray
Mondin et al. Electroless copper deposition on (3-mercaptopropyl) triethoxysilane-coated silica and alumina nanoparticles
Xie et al. Controlled synthesis, characterization, and crystallization of Ni− P nanospheres
Zhang et al. Two-component spin-coated Ag/CNT composite films based on a silver heterogeneous nucleation mechanism adhesion-enhanced by mechanical interlocking and chemical grafting
Chen et al. PET surface modification with inkjet-printing Pd2+/epoxy resin solution for selective electroless copper plating
Yang et al. Preparation and conductive property of Cu coatings and Cu-graphene composite coatings on ABS substrate
Gui et al. Preparation of nickel/PA12 composite particles by defect-induced electroless plating for use in SLS processing
Scarpa et al. Self-assembled monolayers of reduced graphene oxide for robust 3D-printed supercapacitors
Dai et al. Research on the coating formation of Al-induced electroless plating on metallic surfaces
Bragaglia et al. Sustainable formaldehyde-free copper electroless plating on carbon-epoxy substrates
Mehdizadeh et al. Direct electroplating of nickel on ABS plastic using polyaniline–silver surface composite synthesized using different acids
Wang et al. Selective laser melting of ink-printed (SLM-IP) copper (Cu) nanoparticles (NPs) for facile controllable fabrication of super-hydrophobic surface
Chen et al. Polymer Brush Induced Electroless Copper Plating on PA12 Surface for Tensile Strength Enhancement of Selective Laser Sintering Part
Inberg et al. Gold plating of AlSi10Mg parts produced by a laser powder-bed fusion additive manufacturing technique
Lei et al. Controlling the size of silver nanowires through one-pot polyol method with trace halide and its effect on kinetic process
Alehdaghi et al. Facile preparation of various ZnO nanostructures via ultrasonic mist vapor deposition: a systematic investigation about the effects of growth parameters
Kurt et al. Surface functionalization of nano MgO particles with nickel and cobalt
Liu et al. Rationally design of substrate surface topography toward the improvement of Cu-plated coating adhesion