Sol–gel synthesis and characterization of alumina–calcium hexaaluminate composites

Vishista et al., 2005

Document ID
7014451045583980712
Author
Vishista K
Gnanam F
Awaji H
Publication year
Publication venue
Journal of the American Ceramic Society

External Links

Snippet

Boehmite sol was prepared by hot water hydrolysis of aluminum iso‐propoxide using nitric acid as the catalyst. Calcium nitrate to yield 0–20 vol% calcia was added to the boehmite sol. The boehmite with additives was calcined at 600° C for 3 h. The calcined powder was …
Continue reading at ceramics.onlinelibrary.wiley.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C04B2235/3229—Cerium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/628—Coating the powders or the macroscopic reinforcing agents
    • C04B35/62802—Powder coating materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C04B35/645—Pressure sintering
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/48—Organic compounds becoming part of a ceramic after heat treatment, e.g. carbonising phenol resins
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/71—Ceramic products containing macroscopic reinforcing agents
    • C04B35/78—Ceramic products containing macroscopic reinforcing agents containing non-metallic materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment

Similar Documents

Publication Publication Date Title
Ma et al. Nanocrystalline high‐entropy carbide ceramics with improved mechanical properties
Hackett et al. Phase constitution and mechanical properties of carbides in the Ta–C system
Muoto et al. Phase homogeneity in Y 2 O 3–MgO nanocomposites synthesized by thermal decomposition of nitrate precursors with ammonium acetate additions
Kitayama et al. Effect of rare earth oxide additives on the phase transformation rates of Si3N4
Nachiappan et al. Synthesis and densification of monolithic zirconium carbide by reactive hot pressing
Boakye et al. Processing and testing of Re2Si2o7 fiber–matrix interphases for SiC–SiC composites
Sun et al. Synthesis of high entropy carbide ceramics via polymer precursor route
Mecif et al. Preparation of mullite‐and zircon‐based ceramics using kaolinite and zirconium oxide: a sintering study
Perevislov et al. Silicon carbide liquid-phase sintering with various activating agents
Demirskyi et al. High‐strength B4C–TaB2 eutectic composites obtained via in situ by spark plasma sintering
Yan et al. In situ synthesis of ultrafine ZrB2–SiC composite powders and the pressureless sintering behaviors
Sun et al. Reaction sintering of HfC/W cermets with high strength and toughness
Vishista et al. Sol–gel synthesis and characterization of alumina–calcium hexaaluminate composites
Sujith et al. Coarsening induced phase transformation of hafnia in polymer‐derived Si–Hf–C–N–O ceramics
Zaykoski et al. Synthesis and characterization of YB4 ceramics
Liu et al. Lattice rigidity in high‐entropy carbide ceramics with carbon vacancies
Zhou et al. In situ processing and high‐temperature properties of Ti3Si (Al) C2/SiC composites
Yan et al. Near‐net‐size preparation of porous mullite matrix ceramics with in situ formed 3D mullite whisker network
Feng et al. Synthesis, densification, microstructure, and mechanical properties of samarium hexaboride ceramic
Limeng et al. Microstructure and mechanical properties of spark plasma sintered TaC0. 7 ceramics
Liu et al. Temperature‐dependent mechanical and oxidation behavior of in situ formed ZrN/ZrO2‐containing Si3N4‐based composite
Hao et al. High fracture toughness of HfC through nano‐scale templating and novel sintering aids
Tan et al. In situ reaction synthesis of high‐entropy carbide/diboride composite with high mechanical properties
Kaplan Akarsu et al. Comparative study of reactive and nonreactive spark plasma sintering routes for the production of TaB2‐TaC composites
Reddy et al. Insights into the issues during hot‐pressing and vacuum sintering of 10 mol.% CaO doped zirconia ceramics